PC/ABS C7410 GY71197 SABIC INNOVATIVE US
CYCOLAC™ 
Electrical applications,Automotive interior parts,Thin walled components
High mobility,High impact resistance,Filler: Talc filler
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/C7410 GY71197
Charpy Notched Impact Strength23°CISO 179/1eA11 kJ/m²
23°CISO 180/1A31 kJ/m²
ASTM D256320 J/m
-30°CASTM D25671 J/m
ISO 180/1A7.0 kJ/m²
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/C7410 GY71197
fractureISO 527-2/538.0 Mpa
yieldASTM D6383.5 %
ASTM D63854.0 Mpa
Yield, 50.0mm spanASTM D79096.0 Mpa
yieldISO 527-2/558.0 Mpa
ISO 527-2/53.6 %
fractureASTM D63844.0 Mpa
ASTM D63874 %
--8ISO 17895.0 Mpa
50.0mm spanASTM D7903180 Mpa
fractureISO 527-2/578 %
--1ASTM D6383310 Mpa
--7ISO 1783270 Mpa
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/C7410 GY71197
UL flame retardant rating0.00mmUL 945VB
0.800mmUL 94V-0
physical property Test ConditionTest MethodSABIC INNOVATIVE US/C7410 GY71197
melt mass-flow rate260°C/2.16kgASTM D123813 g/10min
Shrinkage rateMD:3.20mm内部方法0.30-0.50 %
Water absorption rate平衡,23°C,50%RHISO 620.060 %
Melt volume flow rate260°C/2.16kgISO 113312.6 cm3/10min
Water absorption rate饱和,23°CISO 620.26 %
Shrinkage rateTD:3.20mm内部方法0.30-0.50 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/C7410 GY71197
Linear coefficient of thermal expansionTD:-40到40°CASTME8316E-05 cm/cm/°C
1.8MPa, Unanealed, 64.0mm spanISO 75-2/Af83.0 °C
1.8MPa, Unanealed, 3.20mmASTM D64880.0 °C
1.8MPa, Unanealed, 6.40mmASTM D64887.0 °C
Linear coefficient of thermal expansionMD:-40到40°CASTME8316E-05 cm/cm/°C