Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
TSU-Ether InnoTuf® HP-2150A Innovative Polymers, Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Uncured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2150A |
|---|---|---|---|
| Viscosity | 固化时间(25°C) | 1.7E+02 hr | |
| GelTime | 20to30 min | ||
| 25°C4 | 0.63 Pa·s | ||
| 25°C2 | 0.13 Pa·s | ||
| 25°C3 | 0.48 Pa·s |
| thermosetting | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2150A |
|---|---|---|---|
| Thermosetting components | 脱模时间 | 300to420 min | |
| 硬化法 | 按重量计算的混合比:47按容量计算的混合比:50 | ||
| 树脂 | 按重量计算的混合比:100按容量计算的混合比:100 |
| Cured Properties | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2150A |
|---|---|---|---|
| tear strength | ASTM D624 | 22.8 kN/m | |
| elongation | 断裂 | ASTM D638 | 600 % |
| tensile strength | ASTM D638 | 5.86 MPa | |
| Shore hardness | ShoreA | ASTM D2240 | 45to55 |
| physical property | Test Condition | Test Method | Innovative Polymers, Inc./InnoTuf® HP-2150A |
|---|---|---|---|
| density | Hardener | 0.990 g/cm³ | |
| 基体树脂 | 1.08 g/cm³ | ||
| Shrinkage rate | MD | ASTM D2566 | 0.20to0.50 % |
| density | Cured | 1.04 g/cm³ |