Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC 3413R-131 SABIC INNOVATIVE NANSHA
LEXAN™
Automotive sector
Glass fiber reinforced、enhance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3413R-131 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D1822 | 67.0 kJ/m² | |
| Dart impact | 23°C | ASTM D3029 | 5.00 J |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3413R-131 |
|---|---|---|---|
| Rockwell hardness | M计秤 | ASTM D785 | 92 |
| R计秤 | ASTM D785 | 120 |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3413R-131 |
|---|---|---|---|
| Dissipation Factor | 50Hz | ASTM D150 | 1.1E-03 |
| 60Hz | ASTM D150 | 1.1E-03 | |
| dielectric constant | 60Hz | ASTM D150 | 3.35 |
| Volume resistivity | ASTM D257 | >1.0E+17 ohms·cm | |
| dielectric constant | 50Hz | ASTM D150 | 3.35 |
| Dissipation Factor | 1MHz | ASTM D150 | 7E-03 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 4 |
| dielectric constant | 1MHz | ASTM D150 | 3.31 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| arc resistance | ASTM D495 | PLC7 | |
| dielectric strength | 3.20mm,inAir | ASTM D149 | 19 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 5 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3413R-131 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.0 % |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 153 Mpa |
| tensile strength | 断裂 | ASTM D638 | 100 Mpa |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | ASTM D1044 | 24.0 mg |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 6610 Mpa |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3413R-131 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| 3.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-1 |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3413R-131 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10-0.30 % |
| Water absorption rate | 24hr | ASTM D570 | 0.14 % |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 19 g/10min |
| Water absorption rate | 平衡,23°C | ASTM D570 | 0.26 % |
| Specific volume | ASTM D792 | 0.697 cm³/g | |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 5.0 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/3413R-131 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 146 °C |
| thermal conductivity | ASTMC177 | 0.22 W/m/K | |
| Linear coefficient of thermal expansion | MD：-40到95°C | ASTME831 | 2.2E-05 cm/cm/°C |
| vicat | ASTM D15255 | 165 °C | |
| RTI Imp | UL 746 | 120 °C | |
| Heat distortion temperature | 0.45MPa,未退火,6.40mm，HDT | ASTM D648 | 151 °C |
| RTI Str | UL 746 | 130 °C | |
| specific heat | ASTMC351 | 1130 J/kg/°C | |
| RTI Elec | UL 746 | 120 °C |