Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 B50H1 SOLVAY SHANGHAI
--
Laptop case、Electronic field、Electrical field、Pipe fittings、currency、pipeline、Profile
High rigidity、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY SHANGHAI/B50H1 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| -30°C | ISO 179/1eU | 80 kJ/m² |
| Supplementary Information | Test Condition | Test Method | SOLVAY SHANGHAI/B50H1 |
|---|---|---|---|
| EuropeanRailwaysCertifications | R22 | EN45545-2 | HL2 |
| R23 | EN45545-2 | HL3 |
| Electrical performance | Test Condition | Test Method | SOLVAY SHANGHAI/B50H1 |
|---|---|---|---|
| relative permittivity | IEC 60250 | 3.60 | |
| Dissipation Factor | IEC 60250 | 0.020 | |
| dielectric strength | 0.800mm | IEC 60243-1 | 33 KV/mm |
| Volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms |
| Mechanical properties | Test Condition | Test Method | SOLVAY SHANGHAI/B50H1 |
|---|---|---|---|
| Tensile modulus | 23°C | ISO 527-2/1A | 3750 Mpa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 12 % |
| bending strength | 23°C | ISO 178 | 130 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.0 % |
| Flexural modulus | 23°C | ISO 178 | 3700 Mpa |
| bending strength | 23°C | ASTM D790 | 125 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2/1A | 70.0 Mpa |
| 屈服,23°C | ASTM D638 | 85.0 Mpa | |
| 屈服,23°C | ISO 527-2/1A | 80.0 Mpa | |
| Flexural modulus | 23°C | ASTM D790 | 3800 Mpa |
| elongation | 断裂,23°C | ASTM D638 | 15 % |
| flammability | Test Condition | Test Method | SOLVAY SHANGHAI/B50H1 |
|---|---|---|---|
| UL flame retardant rating | NFF16-101 | F2 | |
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 960 °C |
| 0.8mm | IEC 60695-2-12 | 960 °C | |
| 3.2mm | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 3.2mm | UL 94 | V-0 |
| 0.8mm | UL 94 | V-0 | |
| GWIT | 1.6mm | IEC 60695-2-13 | 650 °C |
| Limiting Oxygen Index | ISO 4589-2 | 33 % | |
| UL flame retardant rating | 1.6mm | UL 94 | V-0 |
| smoke density | NFF16-101 | I2 | |
| UL flame retardant rating | 0.40mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | SOLVAY SHANGHAI/B50H1 |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 1.1 % |
| Outdoor applicability | UL 746C | f1 | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 3.1 % |
| Thermal performance | Test Condition | Test Method | SOLVAY SHANGHAI/B50H1 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 85.0 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 85.0 °C | |
| melting temperature | ISO 11357-3 | 242 °C |