PPA T1 GF 40 9 black (3499) AKRO-PLASTIC GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 40 9 black (3499) |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| -30°C | ISO 179/1eA | 11 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| -30°C | ISO 179/1eU | 55 kJ/m² |
| Supplementary Information | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 40 9 black (3499) |
|---|---|---|---|
| ReinforcementContent | ISO 1172 | 40 % |
| hardness | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 40 9 black (3499) |
|---|---|---|---|
| ball-indentation hardness | H961/30 | ISO 2039-1 | 310 MPa |
| Mechanical properties | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 40 9 black (3499) |
|---|---|---|---|
| tensile strength | 断裂 | ISO 527-2/5 | 250 MPa |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.4 % |
| Flexural modulus | ISO 178 | 14500 MPa | |
| Fracture bending strain | ISO 178 | 2.9 % | |
| Tensile modulus | ISO 527-2/1 | 15000 MPa | |
| bending strength | ISO 178 | 360 MPa |
| Electrical performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 40 9 black (3499) |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| flammability | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 40 9 black (3499) |
|---|---|---|---|
| burning rate | 1.00mm | FMVSS302 | <100 mm/min |
| Burning wire flammability index | 1.6mm | IEC 60695-2-12 | 675 °C |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| physical property | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 40 9 black (3499) |
|---|---|---|---|
| spiral flow length | 内部方法 | 67.0 cm | |
| density | 23°C | ISO 1183 | 1.52 g/cm³ |
| Shrinkage rate | TD | ISO 294-4 | 0.80 % |
| MD | ISO 294-4 | 0.30 % | |
| Water absorption rate | 70°C | ISO 1110 | 1.1 % |
| Thermal performance | Test Condition | Test Method | AKRO-PLASTIC GmbH/ T1 GF 40 9 black (3499) |
|---|---|---|---|
| TemperatureIndex | 50%LossofTensileStrength,20000hr | IEC 216 | 130to140 °C |
| melting temperature | DIN EN11357-1 | 308 °C | |
| TemperatureIndex | 50%LossofTensileStrength,5000hr | IEC 216 | 150to160 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 275 °C |
| 8.0MPa,未退火，HDT | ISO 75-2/C | 195 °C |