PP EG103AI BOREALIS EUROPE
Daplen™
Automotive sector、Automotive interior parts、Application in the automo、Automotive interior parts
Recyclable、High rigidity、Mineral reinforcement、High impact resistance、High mobility、filler、Mineral filler、15%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | BOREALIS EUROPE/EG103AI |
|---|---|---|---|
| Charpy Notched Impact Strength | -20℃ | ISO 179/1eU | 60 kJ/m² |
| Tensile modulus | ISO 527-2 | 1800 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 22.0 Mpa |
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 49.0 Mpa |
| Flexural modulus | ISO 178 | 1900 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/1 | 5.0 % |
| Charpy Notched Impact Strength | -20℃ | ISO 179/1eA | 3.0 kJ/m² |
| 23℃ | ISO 179/1eU | 150 kJ/m² | |
| 23℃ | ISO 179/1eA | 15 kJ/m² |
| physical property | Test Condition | Test Method | BOREALIS EUROPE/EG103AI |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.9 % | |
| melt mass-flow rate | 230℃/2.16 kg | ISO 1133 | 26 g/10min |
| Thermal performance | Test Condition | Test Method | BOREALIS EUROPE/EG103AI |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 105 °C |
| vicat | ISO 306/B | 54.0 °C | |
| atomization | 100℃, 16 h | VDA 277 | < 60.0 µgC/g |
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 54.0 °C |
| vicat | ISO 306/A | 140 °C |