PC BFL4000 WH3150 SABIC INNOVATIVE US
LEXAN™
Electrical applications、Lighting applications
Thermal stability、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 130 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 7.5E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B120 | 139 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTMD648 | 134 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 124 °C |
| 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 115 °C | |
| Vicat Softening Temperature | -- | ISO306/B50 | 137 °C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm | ASTMD648 | 131 °C |
| Linear thermal expansion coefficient | TD：-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,退火,3.20mm | ASTMD648 | 115 °C |
| Vicat Softening Temperature | ASTMD152510 | 136 °C |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Flexural Modulus | 50.0mm跨距 | ASTMD790 | 2050 Mpa |
| Tensile Elongation | 断裂 | ASTMD638 | 56 % |
| Tensile Strain | 断裂 | ISO527-2/5 | 74 % |
| Tensile Modulus | ISO527-2/1 | 2040 Mpa | |
| Tensile Strength | 屈服 | ASTMD638 | 54.0 Mpa |
| Tensile Stress | 断裂 | ISO527-2/5 | 44.0 Mpa |
| Flexural Modulus | ISO178 | 2170 Mpa | |
| Flexural Strength | 屈服,50.0mm跨距 | ASTMD790 | 90.0 Mpa |
| Tensile Elongation | 屈服 | ASTMD638 | 5.0 % |
| Flexural Strength | ISO178 | 83.0 Mpa | |
| Tensile Modulus | ASTMD638 | 2240 Mpa | |
| Tensile Strength | 断裂 | ASTMD638 | 47.0 Mpa |
| Tensile Strain | 屈服 | ISO527-2/5 | 6.0 % |
| Tensile Stress | 屈服 | ISO527-2/5 | 50.0 Mpa |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.38 g/cm³ | |
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.15 % |
| Density / Specific Gravity | ASTMD792 | 1.38 g/cm³ | |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.50to0.70 % |
| Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 24 g/10min |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 22.0 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.35 % |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 20 kJ/m² |
| 23°C | ASTMD256 | 470 J/m | |
| -30°C | ASTMD256 | 240 J/m | |
| Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 68.0 J |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 30 kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 30 kJ/m² |
| Flammability | Test Condition | Test Method | SABIC INNOVATIVE US/BFL4000 WH3150 |
|---|---|---|---|
| Flame Rating | 1.5mm | UL94 | V-0 |