Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS NH-1017D K23089 LOTTE CHEM DONGGUAN
INFINO®
--
High impact resistance、high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE CHEM DONGGUAN/NH-1017D K23089 |
|---|---|---|---|
| CharpyNotchedImpactStrength5 | 23°C | ISO179/1eA | 14 kJ/m² |
| Suspended wall beam gap impact strength 5 | 23°C | ISO180/1A | 13 kJ/m² |
| hardness | Test Condition | Test Method | LOTTE CHEM DONGGUAN/NH-1017D K23089 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTMD785 | 113 |
| R级 | ISO2039-2 | 113 |
| Mechanical properties | Test Condition | Test Method | LOTTE CHEM DONGGUAN/NH-1017D K23089 |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/50 | 44.0 Mpa |
| 屈服 | ISO527-2/50 | 59.0 Mpa | |
| elongation | 断裂 | ASTMD638 | 8.8 % |
| Flexural modulus | ASTMD790 | 2100 Mpa | |
| tensile strength | 屈服 | ASTMD638 | 53.0 Mpa |
| Flexural Strength | ASTMD790 | 74.0 Mpa | |
| Bending stress | ISO178 | 83.0 Mpa | |
| tensile strength | 断裂 | ASTMD638 | 43.0 Mpa |
| Tensile strain | 断裂 | ISO527-2/50 | 10 % |
| Tensile modulus | ASTMD638 | 2400 Mpa | |
| Flexural modulus | ISO178 | 2350 Mpa | |
| Tensile modulus | ISO527-2/50 | 2400 Mpa |
| flammability | Test Condition | Test Method | LOTTE CHEM DONGGUAN/NH-1017D K23089 |
|---|---|---|---|
| FlameRating | 2.0to3.0mm | UL94 | V-05VB |
| physical property | Test Condition | Test Method | LOTTE CHEM DONGGUAN/NH-1017D K23089 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.20to0.30 % |
| TD:3.20mm | ISO2577 | 0.20to0.40 % | |
| TD：3.20mm | ASTMD955 | 0.20to0.40 % | |
| melt mass-flow rate | 220°C/10.0kg | ISO1133 | 55 g/10min |
| Shrinkage rate | MD:3.20mm | ISO2577 | 0.20to0.30 % |
| melt mass-flow rate | 220°C/10.0kg | ASTMD1238 | 55 g/10min |
| Thermal performance | Test Condition | Test Method | LOTTE CHEM DONGGUAN/NH-1017D K23089 |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,Unannealed,4.00mm | ISO75-2/B | 85.0 °C |
| vicat | ISO306/B50 | 91.0 °C | |
| Heat Deflection Temperature | 1.8MPa,Unannealed,4.00mm | ISO75-2/A | 75.0 °C |
| 1.8MPa,未退火,6.40mm | ASTMD648 | 80.0 °C | |
| 0.45MPa,未退火,6.40mm | ASTMD648 | 87.0 °C | |
| RTI Elec | 2.0mm | UL746 | 85.0 °C |
| RTI Imp | 2.0mm | UL746 | 85.0 °C |
| RTI Str | 2.0mm | UL746 | 85.0 °C |