Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO/PA GTX904-1710 SABIC INNOVATIVE US
NORYL GTX™
Industrial machinery、Electrical applications
Hydrolysis resistance、High temperature resistan、Dimensional stability、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX904-1710 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 20 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 60.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE US/GTX904-1710 |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 85.0 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/GTX904-1710 |
|---|---|---|---|
| tensile strength | 屈服4 | ASTM D638 | 65.0 Mpa |
| elongation | 断裂4 | ASTM D638 | 60 % |
| bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 95.0 Mpa |
| Tensile modulus | --3 | ASTM D638 | 2300 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 25 % |
| Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2350 Mpa |
| bending strength | --6,7 | ISO 178 | 90.0 Mpa |
| Flexural modulus | --6 | ISO 178 | 2200 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 55.0 Mpa |
| 屈服 | ISO 527-2/50 | 65.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 4.5 % |
| 屈服4 | ASTM D638 | 5.0 % | |
| tensile strength | 断裂4 | ASTM D638 | 55.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2400 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/GTX904-1710 |
|---|---|---|---|
| Shrinkage rate | MD:3.20mm | 内部方法 | 1.4-1.7 % |
| melt mass-flow rate | 280°C/5.0kg | ASTM D1238 | 13 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 1.2 % |
| 饱和,23°C | ISO 62 | 3.5 % | |
| Shrinkage rate | TD:3.20mm | 内部方法 | 1.1-1.4 % |
| MD2 | 内部方法 | 1.6-2.0 % | |
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 13.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/GTX904-1710 |
|---|---|---|---|
| thermal conductivity | ISO 8302 | 0.23 W/m/K | |
| Linear coefficient of thermal expansion | TD:23到60°C | ISO 11359-2 | 7E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火,100mm跨距10，HDT | ISO 75-2/Be | 190 °C |
| vicat | -- | ISO 306/A50 | 250 °C |
| Linear coefficient of thermal expansion | MD:23到60°C | ISO 11359-2 | 8E-05 cm/cm/°C |
| TD:-40到40°C | ASTME831 | 8.5E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 190 °C |
| vicat | -- | ISO 306/B50 | 200 °C |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7.5E-05 cm/cm/°C |
| vicat | -- | ASTM D-596 | 205 °C |