Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A9000 宁波德立隆
--
阻燃性,耐热性,电阻性良好
接插件,电子端子,电子元件等
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | 宁波德立隆/A9000 |
|---|---|---|---|
| Tensile strength at break | IS0527 | 75 Mpa | |
| Rockwell hardness | R标尺 | 119 | |
| Impact strength of support beam gap | ISO 179/1eA | 4 kJ/m² | |
| bending strength | IS0178 | 115 Mpa | |
| Simple support without notch impact strength | ISO 179/1eU | NB kJ/m² | |
| Flexural modulus | IS0 178 | 3000 Mpa | |
| elongation at break | IS0 527 | 6 |
| other | Test Condition | Test Method | 宁波德立隆/A9000 |
|---|---|---|---|
| Drying temperature/time | 90/6-10 °C/hr | ||
| Injection molding temperature range | 255-280 °C | ||
| Surface Resistivity | ISO 167 | 10¹² Ohm | |
| Linear forming shrinkage rate | ISO2577 | 0.01-0.014 mm/mm | |
| dielectric strength | IEC 1183 | 18 KV/mm | |
| filler | GF45 % |
| Flame retardant performance | Test Condition | Test Method | 宁波德立隆/A9000 |
|---|---|---|---|
| fire rating | UL94 | V-0 |
| physical property | Test Condition | Test Method | 宁波德立隆/A9000 |
|---|---|---|---|
| Water absorption rate | 24hr，23°C | IS0 62 | 1.1 % |
| density | ISO 1183 | 1.18 g/cm³ |
| Thermal performance | Test Condition | Test Method | 宁波德立隆/A9000 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa | IS075 | 170 ℃ |
| 1.82MPa | IS0 75 | 100 ℃ |