PBT GP1000DS DKA02 LG CHEM KOREA
LUPOX®
Application in the automo
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LG CHEM KOREA/GP1000DS DKA02 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,6.40mm | ASTM D256 | 51 J/m |
| Electrical performance | Test Condition | Test Method | LG CHEM KOREA/GP1000DS DKA02 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+17 ohms·cm | |
| arc resistance | ASTM D495 | PLC 5 | |
| dielectric strength | 1.00mm | ASTM D149 | 23 KV/mm |
| Compared to the Leakage Tracking Index (CTI) | CTI)5 | UL 746 | PLC 0 |
| 解决方案A | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | LG CHEM KOREA/GP1000DS DKA02 |
|---|---|---|---|
| elongation | 断裂,3.20mm | ASTM D638 | >100 % |
| tensile strength | 屈服,3.20mm | ASTM D638 | 46.1 Mpa |
| Flexural modulus | 3.20mm | ASTM D790 | 1860 Mpa |
| bending strength | 屈服,3.20mm | ASTM D790 | 65.7 Mpa |
| flammability | Test Condition | Test Method | LG CHEM KOREA/GP1000DS DKA02 |
|---|---|---|---|
| UL flame retardant rating | 3.3mm | UL 94 | HB |
| 1.5mm | UL 94 | HB | |
| 0.71mm | UL 94 | HB |
| physical property | Test Condition | Test Method | LG CHEM KOREA/GP1000DS DKA02 |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 34 g/10min |
| Shrinkage rate | MD | ASTM D955 | 1.2-2.0 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.080 % |
| density | ASTM D792 | 1.29 g/cm³ |
| Thermal performance | Test Condition | Test Method | LG CHEM KOREA/GP1000DS DKA02 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 57.0 °C |
| melting temperature | ASTM D3418 | 223 °C | |
| RTI Imp | UL 746 | 130 °C | |
| RTI | UL 746 | 140 °C | |
| RTI Elec | UL 746 | 140 °C |