ASA XTWM206-BK1C091 SABIC INNOVATIVE US
GELOY™ 
Electronic and electrical、Lawn garden equipment、High temperature applicat
Colorable、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/XTWM206-BK1C091
Linear thermal expansion coefficient流动 : -40 到 40°CISO 11359-28.3E-5 cm/cm/°C
Deflection Temperature Under Load?1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 11ISO 75-2/Af84.0 °C
Linear thermal expansion coefficient横向 : -40 到 40°CASTM E8319.4E-5 cm/cm/°C
横向 : -40°CISO 11359-29.4E-5 cm/cm/°C
Vicat Softening Temperature--ISO 306/B5095.0 °C
--ISO 306/B12099.0 °C
Deflection Temperature Under Load?0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 11ISO 75-2/Bf98.0 °C
1.8 MPa, 未退火, 3.20 mmASTM D64884.0 °C
Linear thermal expansion coefficient流动 : -40 到 40°CASTM E8318.4E-5 cm/cm/°C
Deflection Temperature Under Load?0.45 MPa, 未退火, 3.20 mmASTM D64897.0 °C
Vicat Softening Temperature--98.0 °C
Ball PressureTest83 到 87°CIEC 60695-10-2通过
HardnessTest ConditionTest MethodSABIC INNOVATIVE US/XTWM206-BK1C091
Rockwell HardnessR 级ASTM D785100
InjectionTest ConditionTest MethodSABIC INNOVATIVE US/XTWM206-BK1C091
Middle Temperature220 到 255 °C
Drying Time4.0 hr
Suggested Shot Size40 到 80 %
Drying Temperature85 到 90 °C
Mold Temperature60 到 85 °C
Vent Depth0.038 到 0.076 mm
Suggested Max Moisture0.040 %
Processing (Melt) Temp240 到 270 °C
Rear Temperature215 到 250 °C
Nozzle Temperature220 到 255 °C
Front Temperature230 到 260 °C
Back Pressure0.300 到 1.00 Mpa
Screw Speed30 到 80 rpm
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/XTWM206-BK1C091
Melt Mass-Flow Rate260°C/5.0 kgASTM D12387.1 g/10 min
Moisture Absorption平衡, 23°C, 50% RHISO 620.20 %
Melt Mass-Flow Rate220°C/10.0 kgASTM D12388.8 g/10 min
280°C/3.8 kgASTM D12387.2 g/10 min
Outdoor SuitabilityUL 746Cf1
Modeling Shrinkage流动  2内部方法0.40 到 0.70 %
横向流动 : 3.20 mm内部方法0.40 到 0.75 %
Melt Volume flow Rate260°C/5.0 kgISO 11339.00 cm3/10min
Modeling Shrinkage流动 : 3.20 mm内部方法0.40 到 0.70 %
Moisture Absorption饱和, 23°CISO 620.50 %
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/XTWM206-BK1C091
Tensile Strength断裂ISO 527-2/5036.0 Mpa
Tensile Modulus--ISO 527-2/12350 Mpa
Tensile Elongation屈服 6ASTM D6382.5 %
断裂 5ASTM D63826 %
Flexural Stress-- 8, 9ISO 17864.0 Mpa
Flexural Modulus50.0 mm 跨距 7ASTM D7902450 Mpa
Flexural Stress屈服, 50.0 mm 跨距 7ASTM D79074.0 Mpa
Tensile Elongation屈服ISO 527-2/502.8 %
Tensile Strength屈服 5ASTM D63846.0 Mpa
屈服 6ASTM D63843.0 Mpa
屈服ISO 527-2/5045.0 Mpa
Tensile Modulus-- 3ASTM D6382360 Mpa
-- 4ASTM D6382400 Mpa
Tensile Strength断裂 5ASTM D63837.0 Mpa
Tensile Elongation断裂 6ASTM D63827 %
屈服 5ASTM D6382.7 %
Flexural Modulus-- 8ISO 1782380 Mpa
Tensile Strength断裂 6ASTM D63836.0 Mpa
Tensile Elongation断裂ISO 527-2/5036 %
OpticalTest ConditionTest MethodSABIC INNOVATIVE US/XTWM206-BK1C091
Gardner60°, 无织构ASTM D52393
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/XTWM206-BK1C091
Instrumented Dart Impact23°C, Total EnergyASTM D376336.0 J
-30°C, Total EnergyASTM D37633.00 J
FlammabilityTest ConditionTest MethodSABIC INNOVATIVE US/XTWM206-BK1C091
UL flame retardant rating1.5 mmUL 94HB