PBT PRL TP-FR-IM Polymer Resources Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Polymer Resources Ltd./PRL TP-FR-IM |
|---|---|---|---|
| Dart impact | 3.18mm | ASTM D3029 | >36.2 J |
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTM D256 | 530 J/m |
| Electrical performance | Test Condition | Test Method | Polymer Resources Ltd./PRL TP-FR-IM |
|---|---|---|---|
| dielectric strength | 0.850mm | ASTM D149 | 27 kV/mm |
| arc resistance | 0.850mm | ASTM D495 | PLC6 |
| Volume resistivity | ASTM D257 | 1E+14 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 0.850mm | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | 1.6mm | UL 746 | PLC 3 |
| High arc combustion index (HAI) | 0.9mm | UL 746 | PLC 0 |
| 1.6mm | UL 746 | PLC 0 | |
| High Voltage Arc Traceability Rate (HVTR) | 0.850mm | UL 746 | PLC 3 |
| Hot wire ignition (HWI) | 0.9mm | UL 746 | PLC 4 |
| 3.0mm | UL 746 | PLC 2 | |
| High arc combustion index (HAI) | 3.0mm | UL 746 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | Polymer Resources Ltd./PRL TP-FR-IM |
|---|---|---|---|
| Flexural modulus | 3.17mm | ASTM D790 | 2070 MPa |
| tensile strength | 屈服,3.17mm | ASTM D638 | 44.8 MPa |
| Break,3.18mm | ASTM D638 | 44.8 MPa | |
| bending strength | Break,3.18mm | ASTM D790 | 77.9 MPa |
| flammability | Test Condition | Test Method | Polymer Resources Ltd./PRL TP-FR-IM |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 0.9mm | UL 94 | V-0 | |
| 1.6mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | Polymer Resources Ltd./PRL TP-FR-IM |
|---|---|---|---|
| melt mass-flow rate | 250°C/2.16kg | ASTM D1238 | 3.0to9.0 g/10min |
| Shrinkage rate | MD | ASTM D955 | 1.0to1.4 % |
| Outdoor applicability | UL 746C | f2 | |
| density | ASTM D792 | 1.34 g/cm³ |
| Thermal performance | Test Condition | Test Method | Polymer Resources Ltd./PRL TP-FR-IM |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.18mm，HDT | ASTM D648 | 132 °C |
| RTI Imp | 0.9mm | UL 746 | 85.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,3.18mm，HDT | ASTM D648 | 87.8 °C |
| RTI Imp | 1.6mm | UL 746 | 85.0 °C |
| RTI Str | 3.0mm | UL 746 | 130 °C |
| 0.9mm | UL 746 | 130 °C | |
| 1.6mm | UL 746 | 130 °C | |
| RTI Elec | 1.6mm | UL 746 | 130 °C |
| 3.0mm | UL 746 | 130 °C | |
| RTI Imp | 3.0mm | UL 746 | 110 °C |
| RTI Elec | 0.9mm | UL 746 | 130 °C |