Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DX02437 SABIC INNOVATIVE NANSHA
LNP™ STAT-KON™ 
Automotive components,Electronic and electrical accessories
Thermal stability,Low temperature resistanc,Filler: carbon powder
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/DX02437
Charpy Notched Impact Strength23°CISO 179/1eA26 kJ/m²
0°CASTM D256290 J/m
23°CISO 180/1A25 kJ/m²
ISO 180/1U130 kJ/m²
ASTM D256360 J/m
Impact strength of simply supported beam without notch23°CISO 179/1eU95 kJ/m²
23°CASTM D48122100 J/m
23°C,TotalEnergyASTM D376339.1 J
0°CISO 180/1A20 kJ/m²
23°C,EnergyatPeakLoadASTM D376327.0 J
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE NANSHA/DX02437
fractureISO 527-2/547.0 Mpa
ASTM D63819 %
--2ASTM D6382570 Mpa
yieldASTM D63858.0 Mpa
bending strength--8ISO 17892.0 Mpa
Flexural modulusISO 1782550 Mpa
bending strength--9ISO 17890.0 Mpa
yieldISO 527-2/558.0 Mpa
fractureASTM D63847.0 Mpa
Fracture bending strainISO 1787.8 %
fractureISO 527-2/517 %
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/DX02437
Volume resistivityASTM D2571.4E+07 ohms·cm
Surface ResistivityASTM D2574.8E+07 ohms
physical property Test ConditionTest MethodSABIC INNOVATIVE NANSHA/DX02437
Shrinkage rateMD内部方法0.64 %
Melt volume flow rate300°C/5.0kgISO 113316.0 cm3/10min
Shrinkage rateTD内部方法0.68 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE NANSHA/DX02437
vicatISO 306/A50144 °C
1.8MPa, Unanealed, 64.0mm spanISO 75-2/Af126 °C
1.8MPa, Unanealed, 3.20mmASTM D648111 °C