ABS ER460 LG YX NINGBO
--
Automotive sector、Electrical field、Electronic field、Application in the automo
Moderate heat resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | LG YX NINGBO/ER460 |
|---|---|---|---|
| Rockwell hardness | ISO2039-2 | 112 | |
| R级 | ASTMD785 | 110 |
| Mechanical properties | Test Condition | Test Method | LG YX NINGBO/ER460 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO527-2/50 | 45.0 Mpa |
| Tensile modulus | ISO527-2/1 | 2200 Mpa | |
| Flexural Strength3 | 3.20mm | ASTMD790 | 76.5 Mpa |
| elongation | 断裂,3.20mm | ASTMD638 | 15 % |
| Bending stress | ISO178 | 65.0 Mpa | |
| Flexural modulus | ISO178 | 2300 Mpa | |
| 3.20mm | ASTMD790 | 2550 Mpa | |
| tensile strength | 屈服,3.20mm | ASTMD638 | 45.1 Mpa |
| physical property | Test Condition | Test Method | LG YX NINGBO/ER460 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.40to0.70 % |
| melt mass-flow rate | 220°C/10.0kg | ISO1133 | 23 g/10min |
| Shrinkage rate | MD：3.20mm | ISO294-4 | 0.40to0.70 % |
| melt mass-flow rate | 220°C/10.0kg | ASTMD1238 | 22 g/10min |
| Thermal performance | Test Condition | Test Method | LG YX NINGBO/ER460 |
|---|---|---|---|
| Hot deformation temperature 5 | 1.8MPa,Unannealed,4.00mm | ISO75-2/Af | 82.0 °C |
| vicat | ISO306/B50 | 100 °C | |
| Hot deformation temperature 5 | 0.45MPa,Unannealed,4.00mm | ISO75-2/Bf | 89.0 °C |
| Heat distortion temperature | 1.8MPa,未退火,6.40mm | ASTMD648 | 90.0 °C |
| vicat | ASTMD15256 | 97.0 °C |