Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT V3900WX-BK1066 SABIC INNOVATIVE SHANGHAI
VALOX™
Automotive sector、Charging station、Electronic and electrical、Lighting applications、Communication equipment、Wire and cable
High impact、Low warpage、Dimensional stability、High toughness、Weather resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-BK1066 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 800 J/m |
| Instrumented dart impact energy 23 ℃ (73 ℉) total energy | ASTM D3763 | 50 J | |
| Impact strength of cantilever beam gap | 80*10*4，30℃ | ISO 180/1A | 8 kJ/m² |
| Instrumented dart impact energy -40 ℃ (-40 ℉) total energy | ASTM D3763 | 50 J | |
| Impact strength of cantilever beam gap | 80*10*4，23℃ | ISO 180/1A | 45 kJ/m² |
| Charpy Notched Impact Strength | V-notch，23℃ | ISO 179/1eA | 52 kJ/m² |
| Impact strength of cantilever beam gap | 30℃ | ASTM D256 | 110 J/m |
| Electrical Property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-BK1066 |
|---|---|---|---|
| UV exposure, water exposure test, and immersion | UL 746C | F1 | |
| Glow wire ignition temperature (GWIT) | 3.0mm | IEC 60695-2-13 | 725 by VDE |
| 1.0mm | IEC 60695-2-13 | 825 | |
| Glow wire combustion index (GWFI) | 3mm | IEC 60695-2-12 | 960 passes |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-BK1066 |
|---|---|---|---|
| tensile strength | Type I, 50，屈服 | ASTM D638 | 53 Mpa |
| elongation at break | Type I, 50 | ASTM D638 | 50 |
| elongation | Type I, 50，屈服 | ASTM D638 | 5 |
| elongation at break | 50 mm/m | ISO 527 | 42 |
| Flexural modulus | 1.3 mm/m | ASTM D790 | 2200 Mpa |
| tensile strength | 屈服 | Internal | 48 Mpa |
| bending strength | 2 mm/m，屈服 | ISO 178 | 73 Mpa |
| Tensile modulus | 1 mm/mi | ISO 527 | 2090 Mpa |
| bending strength | 1.3 mm，屈服 | ASTM D790 | 80 Mpa |
| tensile strength | 50 mm/m，断裂 | ISO 527 | 40 Mpa |
| elongation at break | ASTM D638 | 250 | |
| Tensile modulus | 5 mm/mi | ASTM D638 | 2200 Mpa |
| Flexural modulus | 2 mm/m | ISO 178 | 2130 Mpa |
| elongation | 50 mm/m，屈服 | ISO 527 | 4 |
| tensile strength | 50 mm/m，屈服 | ISO 527 | 51 Mpa |
| Type I, 50，断裂 | ASTM D638 | 43 Mpa |
| combustibility | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-BK1066 |
|---|---|---|---|
| UL flame retardant rating | 5VA | UL 94 | 3 mm |
| UL fire rating V | UL 94 | 1.5 mm | |
| Glow wire combustion index (GWFI) | 1mm | IEC 60695-2-12 | 960 passes at |
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-BK1066 |
|---|---|---|---|
| vicat | Rate B/5 | ISO 306 | 121 °C |
| Linear coefficient of thermal expansion | -40°C to 4，流动 | ASTM E831 | 88.4 E-6 °C |
| -40°C to 4，横向 | ASTM E831 | 89.7 E-6 °C | |
| RTI Imp | UL 746B | 120 °C | |
| vicat | Rate B/50 | ASTM D1525 | 105 °C |
| Ball indentation temperature | Pass | IEC 60695-10-2 | 125 °C |
| Linear coefficient of thermal expansion | -40°C to 4，流动 | ISO 11359-2 | 88.4 E-6 °C |
| -40°C to 4，横向 | ISO 11359-2 | 89.7 E-6 °C | |
| RTI Elec | UL 746B | 120 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/V3900WX-BK1066 |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238 | 35 g/10min | |
| Water absorption rate | 23°C/sat | ISO 62 | 0.1 |
| 23°C / 50 | ISO 62 | 0.03 | |
| Shrinkage rate | flow, 3.2 | Internal | 0.7-1 |
| Melt volume flow rate | ISO 1133 | 11 cm³/10 min |