Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 西班牙Grupo Repol/A1S25 C10-4152 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | 西班牙Grupo Repol/A1S25 C10-4152 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/5 | 150 MPa |
| 断裂 | ISO 527-2/5 | 150 MPa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 2.5 % |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.0 kJ/m² |
| Tensile strain | 断裂 | ISO 527-2/5 | 2.5 % |
| Flexural modulus | ISO 178 | 7200 MPa | |
| Tensile modulus | ISO 527-2/1 | 9000 MPa | |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eU | 30 kJ/m² |
| bending strength | ISO 178 | 185 MPa |
| Electrical performance | Test Condition | Test Method | 西班牙Grupo Repol/A1S25 C10-4152 |
|---|---|---|---|
| Surface Resistivity | ASTM D257 | <1.0E+4 ohms |
| physical property | Test Condition | Test Method | 西班牙Grupo Repol/A1S25 C10-4152 |
|---|---|---|---|
| Humidity | ISO 15512/B | <0.25 % | |
| density | ISO 1183 | 1.21 g/cm³ |
| Thermal performance | Test Condition | Test Method | 西班牙Grupo Repol/A1S25 C10-4152 |
|---|---|---|---|
| vicat | ISO 306 | >230 °C | |
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ISO 75-2/A | 242 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 242 °C |