PC L-1225Y HF10940Y TEIJIN JAPAN
PANLITE®
Electrical appliances、Casters、Household appliances、Mechanical components、Medical supplies、Labor protection equipmen、container、Electronic field、Electrical field、Application in the automo、Car headlights
Low viscosity、transparent、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225Y HF10940Y |
|---|---|---|---|
| Evolution Calendar intelligent importer | 1.5mm | UL746 | 115 °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 7E-05 cm/cm/°C |
| RTIElec | 1.5mm | UL746 | 125 °C |
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO75-2/B | 136 °C |
| RTIStr | 1.5mm | UL746 | 125 °C |
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO75-2/A | 123 °C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 7E-05 cm/cm/°C |
| Vicat Softening Temperature | ISO306/B50 | 142 °C |
| Physical | Test Condition | Test Method | TEIJIN JAPAN/L-1225Y HF10940Y |
|---|---|---|---|
| Density / Specific Gravity | ISO1183 | 1.20 g/cm³ | |
| Melt Volume flow Rate | 300°C/1.2kg | ISO1133 | 25.0 cm3/10min |
| Modeling Shrinkage | TD:4.00mm | 内部方法 | 0.50to0.70 % |
| MD:4.00mm | 0.50to0.70 % | ||
| Moisture Absorption | 23°C,24hr | ISO62 | 0.20 % |
| Mechanical Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225Y HF10940Y |
|---|---|---|---|
| Flexural Modulus | ISO178 | 2400 Mpa | |
| Tensile Stress | 屈服 | ISO527-2/50 | 62.0 Mpa |
| Tensile Strain | 6.0 % | ||
| Tensile Modulus | ISO527-2/1 | 2400 Mpa | |
| Nominal Tensile Strain at Break | ISO527-2/50 | >50 % | |
| Flexural Stress | ISO178 | 95.0 Mpa |
| Optical | Test Condition | Test Method | TEIJIN JAPAN/L-1225Y HF10940Y |
|---|---|---|---|
| Index of Refraction | ASTMD542 | 1.585 | |
| Transmittance | 3000µm | ASTMD1003 | 88.0 % |
| Impact Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225Y HF10940Y |
|---|---|---|---|
| Charpy Unnotched Impact Strength | ISO179 | NoBreak | |
| Charpy Notched Impact Strength | 53 kJ/m² |
| Flammability | Test Condition | Test Method | TEIJIN JAPAN/L-1225Y HF10940Y |
|---|---|---|---|
| Glow Wire Ignition Temperature | 3.2mm | IEC60695-2-13 | 875 °C |
| Flame Rating | 0.40mm | UL94 | V-2 |
| Glow Wire Flammability Index | 1.5mm | IEC60695-2-12 | 825 °C |
| 3.2mm | 875 °C | ||
| Flame Rating | 2.1mm | UL94 | HB |
| Glow Wire Ignition Temperature | 1.5mm | IEC60695-2-13 | 850 °C |
| Electrical Properties | Test Condition | Test Method | TEIJIN JAPAN/L-1225Y HF10940Y |
|---|---|---|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.10 |
| Dielectric Strength | IEC60243-1 | 30 KV/mm | |
| Dissipation Factor? | 1MHz | IEC60250 | 9E-03 |
| Volume Resistivity | IEC60093 | >1.0E+15 ohms·cm | |
| Comparative Tracking Index | IEC60112 | 250 V | |
| Surface Resistivity | IEC60093 | >1.0E+15 ohms | |
| Relative Permittivity | 1MHz | IEC60250 | 3.00 |
| Dissipation Factor? | 100Hz | 1E-03 |