PA9T G1302 BK KURARAY JAPAN
Genestar™
Electronic field、Electrical field
Low friction coefficient、wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | KURARAY JAPAN/G1302 BK |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 4.0 % |
| bending strength | ASTM D790 | 210 Mpa | |
| Flexural modulus | ASTM D790 | 9000 Mpa | |
| tensile strength | ASTM D638 | 165 Mpa |
| Electrical performance | Test Condition | Test Method | KURARAY JAPAN/G1302 BK |
|---|---|---|---|
| Dissipation Factor | 10.0 GHz | ASTM D150 | 9.0E-3 |
| Volume resistivity | ASTM D257 | 1.0E+16 ohms·cm | |
| dielectric constant | 10.0 GHz | ASTM D150 | 3.30 |
| dielectric strength | ASTM D149 | 30 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | KURARAY JAPAN/G1302 BK |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| elongation at break | ASTM D638 | 0.70 % | |
| Weld Strength | ASTM D638 | 47.0 Mpa | |
| Bar Flow Length | 320°C, 500.0 µm | 5.50 CM |
| physical property | Test Condition | Test Method | KURARAY JAPAN/G1302 BK |
|---|---|---|---|
| Water absorption rate | 平衡, 40°C, 95%RH | 1.4 % | |
| Shrinkage rate | 流动 : 1.00 mm | 0.20 % | |
| 横向流动 : 1.00 mm | 0.70 % | ||
| melt mass-flow rate | 320°C/2.16 kg | ASTM D1238 | 46 g/10 min |
| Thermal performance | Test Condition | Test Method | KURARAY JAPAN/G1302 BK |
|---|---|---|---|
| Glass Transition Temperature | 125 °C | ||
| Heat distortion temperature | 1.8 MPa, 未退火，HDT | ASTM D648 | 290 °C |
| melting temperature | 306 °C |