Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC HL-3003 MITSUBISHI GAS SHANGHAI
IUPILON™ 
Automotive components、Special for cast film、Application in the automo
High temperature resistan、wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/HL-3003
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/HL-3003
Tensile modulusISO 527-22400 Mpa
Nominal tensile fracture strainISO 527-2110 %
bending strengthISO 17898.0 Mpa
Flexural modulusISO 1782300 Mpa
Tensile strain屈服ISO 527-25.8 %
tensile strength 屈服ISO 527-263.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/HL-3003
dielectric strength1.00mmIEC 60243-131 KV/mm
Volume resistivityIEC 600933E+16 ohms·cm
relative permittivity100HzIEC 602503.10
Dissipation Factor100HzIEC 602506E-04
dielectric strength3.00mmIEC 60243-118 KV/mm
relative permittivity1MHzIEC 602503.10
Surface ResistivityIEC 600936E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
Dissipation Factor1MHzIEC 602509E-03
physical property Test ConditionTest MethodMITSUBISHI GAS SHANGHAI/HL-3003
Shrinkage rateTD:3.20mm0.50-0.70 %
吸水率(饱和,23°C)0.24 %
Melt volume flow rate300°C/1.2kgISO 113332.0 cm3/10min
Shrinkage rateMD:3.20mm0.50-0.70 %
melt mass-flow rate300°C/1.2kgISO 113334 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI GAS SHANGHAI/HL-3003
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B137 °C
1.8MPa,未退火，HDTISO 75-2/A123 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
TDISO 11359-26.6E-05 cm/cm/°C