Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

ABS PA-717K ZHENJIANG CHIMEI
POLYLAC®
fibre
high strength、High mobility、High gloss、High temperature resistan、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717K |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179 | 27 kJ/m² |
Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256 | 290 J/m |
23°C,6.40mm | ASTM D256 | 250 J/m | |
Charpy Notched Impact Strength | -30°C | ISO 179 | 13 kJ/m² |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 12 kJ/m² |
23°C | ISO 180/1A | 25 kJ/m² |
hardness | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717K |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 115 |
Mechanical properties | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717K |
---|---|---|---|
tensile strength | 屈服 | ISO 527-2/50 | 44.0 Mpa |
elongation | 断裂4 | ASTM D638 | 30 % |
bending strength | --5 | ASTM D790 | 70.3 Mpa |
tensile strength | 屈服4 | ASTM D638 | 42.1 Mpa |
bending strength | --6 | ISO 178 | 69.0 Mpa |
elongation | 断裂 | ISO 527-2/50 | 30 % |
Flexural modulus | --6 | ISO 178 | 1900 Mpa |
--5 | ASTM D790 | 2410 Mpa | |
tensile strength | 断裂 | ISO 527-2/50 | 33.0 Mpa |
flammability | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717K |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717K |
---|---|---|---|
density | 23°C | ISO 1183 | 1.04 g/cm³ |
melt mass-flow rate | 200°C/5.0kg | ASTM D1238 | 1.3 g/10min |
Shrinkage rate | ISO 294-4 | 0.40-0.70 % | |
density | --3 | ASTM D792 | 1.04 g/cm³ |
Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 16.0 cm3/10min |
Thermal performance | Test Condition | Test Method | ZHENJIANG CHIMEI/PA-717K |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 85.0 °C |
1.8MPa,退火,HDT | ASTM D648 | 95.0 °C | |
vicat | -- | ASTM D15257 | 104 °C |
-- | ISO 306/A50 | 103 °C | |
Heat distortion temperature | 1.8MPa,退火,HDT | ISO 75-2/A | 97.0 °C |
vicat | -- | ISO 306/B50 | 98.0 °C |
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 82.0 °C |
Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.8E-05 cm/cm/°C |