Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PPO GFN30-701S SABIC INNOVATIVE SHANGHAI

NORYL™

Lawn equipment,Garden equipment,Non specific food,Outdoor applications,Electrical field,Electronic field,Architectural application field,Liquid handling,Electrical appliances,Engine hood parts,Medical supplies,Nursing supplies,Plastic bag,Automotive External Parts,Lighting applications

enhance,Glass fiber reinforced,Hydrolysis resistance

Plastic Datasheets

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/GFN30-701S
Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	147 °C
		1.8 MPa, Unannealed, 3.20 mm	ASTM D648	139 °C
		1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span8	ISO 75-2/Af	139 °C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ISO 11359-2	2.3E-5 cm/cm/°C
		Across Flow : -40 to 40°C	ASTM E831	7.5E-5 cm/cm/°C
		Across Flow : -40°C	ISO 11359-2	7.0E-5 cm/cm/°C
		Flow : -40 to 40°C	ASTM E831	2.1E-5 cm/cm/°C
Vicat softening temperature	--	ASTM D15259	147 °C
Vicat softening temperature		--	ISO 306/B120	149 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/GFN30-701S
Bending modulus	50.0 mm Span4	ASTM D790	7200 Mpa
Bending modulus		--5	ISO 178	6800 Mpa
bending strength	Yield, 50.0 mm Span4	ASTM D790	160 Mpa
bending strength		--5,6	ISO 178	160 Mpa
elongation	Break3	ASTM D638	3.0 %
elongation		Break	ISO 527-2/50	2.5 %
Tensile modulus	--2	ASTM D638	8600 Mpa
Tensile modulus		--	ISO 527-2/1	8200 Mpa
tensile strength	Break3	ASTM D638	130 Mpa
tensile strength		Break	ISO 527-2/50	110 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/GFN30-701S
melt mass-flow rate	280°C/5.0 kg	ASTM D1238	3.2 g/10 min
Melt Volume Flow Rate (MVR)	280°C/5.0 kg	ISO 1133	2.00 cm3/10min
Shrinkage rate	3.20 mm，Flow	Internal Method	0.10 - 0.40 %
Water absorption rate	Saturation, 23°C	ISO 62	0.10 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	0.040 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/GFN30-701S
Dart impact	23°C, Total Energy	ASTM D3763	20.0 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	590 J/m
Suspended wall beam without notch impact strength		23°C8	ISO 180/1U	30 kJ/m²

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/GFN30-701S
Back pressure			0.300 to 0.700 Mpa
drying temperature			110 to 120 °C
drying time			3.0 to 4.0 hr
Mold temperature			80 to 110 °C
Processing (melt) temperature			300 to 325 °C
Screw speed			20 to 100 rpm
Spray nozzle temperature			300 to 325 °C
Suggested injection volume			30 to 70 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			290 to 325 °C
Temperature at the rear of the barrel			265 to 315 °C
Temperature in the middle of the barrel			275 to 320 °C