PA66 FG133F1 NC010 DUPONT USA
Zytel®
Non specific food
Non enhanced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| thermal performance | Test Condition | Test Method | DUPONT USA/FG133F1 NC010 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8 MPa, 未退火，HDT | ISO 75-2/A | 78.0 °C |
| melting temperature | ISO 11357-3 | 262 °C |
| Mechanical properties | Test Condition | Test Method | DUPONT USA/FG133F1 NC010 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3800 Mpa | |
| Nominal tensile fracture strain | ISO 527-2 | 14 % | |
| tensile strength | 屈服 | ISO 527-2 | 94.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 6.0 % |
| Physical properties | Test Condition | Test Method | DUPONT USA/FG133F1 NC010 |
|---|---|---|---|
| shrinkage rate | 流量 | ISO 294-4 | 0.80 % |
| 横向流量 | ISO 294-4 | 1.0 % |
| flammability | Test Condition | Test Method | DUPONT USA/FG133F1 NC010 |
|---|---|---|---|
| FMVSS combustion rate | FMVSS 302 | B | |
| burning rate | 1.00 mm | ISO 3795 | < 100 mm/min |
| Filling analysis | Test Condition | Test Method | DUPONT USA/FG133F1 NC010 |
|---|---|---|---|
| Ejection Temperature | 190 °C |
| squeeze out | Test Condition | Test Method | DUPONT USA/FG133F1 NC010 |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Melt Temperature | 235 to 250 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.060 % | ||
| Extrusion Melt Temperature, Optimum | 240 °C |
| injection | Test Condition | Test Method | DUPONT USA/FG133F1 NC010 |
|---|---|---|---|
| pressure holding | 50.0 to 100 Mpa | ||
| Maximum Screw Tangential Speed | 24 m/min | ||
| pressure holding | Drying Recommended | yes | |
| Suggested maximum moisture content | 0.20 % | ||
| Drying time - hot air dryer | 2.0 to 4.0 hr | ||
| Processing (melt) temperature | 280 to 300 °C | ||
| mold temperature | 50 to 90 °C | ||
| drying temperature | 80 °C | ||
| Melt Temperature, Optimum | 290 °C | ||
| Hold Pressure Time | 4.00 s/mm | ||
| Mold Temperature, Optimum | 70 °C |