Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PA66 R513H BK ASCEND USA

Vydyne®

Electrical appliances,Laptop case,Parts box,Lighting applications,switch,Electrical enclosure,Electrical components

Lubricity,Thermal stability,Oil resistant,Antichemical,High mobility,Antisolvent,high strength,High rigidity

Plastic Datasheets

thermal performance	Test Condition	Test Method	ASCEND USA/R513H BK
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	258 °C
Hot deformation temperature		1.8 MPa, Unannealed	ISO 75-2/A	240 °C
Linear coefficient of thermal expansion	Across Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	1.1E-4 cm/cm/°C
Linear coefficient of thermal expansion		Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	3.0E-5 cm/cm/°C
Melting temperature		ISO 11357-3	260 °C
RTI	0.75 mm	UL 746	125 °C
		3.0 mm	UL 746	140 °C
		1.5 mm	UL 746	140 °C
RTI Elec	0.75 mm	UL 746	140 °C
		1.5 mm	UL 746	140 °C
		3.0 mm	UL 746	140 °C
RTI Imp	3.0 mm	UL 746	120 °C
		1.5 mm	UL 746	120 °C
		0.75 mm	UL 746	120 °C

mechanical properties	Test Condition	Test Method	ASCEND USA/R513H BK
Bending modulus	23°C	ISO 178	5200 Mpa
bending strength	23°C	ISO 178	165 Mpa
Poisson's ratio		ISO 527-2	0.40
Tensile modulus	23°C	ISO 527-2	6200 Mpa
Tensile strain	Break, 23°C	ISO 527-2	3.0 %
tensile strength	Break, 23°C	ISO 527-2	115 Mpa

Electrical performance	Test Condition	Test Method	ASCEND USA/R513H BK
Arc resistance	3.00 mm	ASTM D495	PLC 6
Compared to the anti leakage trace index	3.00 mm	IEC 60112	V
Dielectric strength	1.00 mm	IEC 60243	20 KV/mm
High arc combustion index	1.5 mm	UL 746	PLC 0
		3.0 mm	UL 746	PLC 0
		0.75 mm	UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 1
Hot wire ignition	0.75 mm	UL 746	PLC 4
		1.5 mm	UL 746	PLC 3
		3.0 mm	UL 746	PLC 4
Volume resistivity	0.750 mm	IEC 60093	1.0E+13 ohms·cm

Physical properties	Test Condition	Test Method	ASCEND USA/R513H BK
Shrinkage rate	Flow : 23°C, 2.00 mm	ISO 294-4	0.50 %
Shrinkage rate		横向Flow : 23°C, 2.00 mm	ISO 294-4	1.0 %
Water absorption rate	24 hr, 23°C	ISO 62	1.0 %
Water absorption rate		Equilibrium, 23°C, 50% RH	ISO 62	2.2 %

impact performance	Test Condition	Test Method	ASCEND USA/R513H BK
Impact strength of simply supported beam without notch	-30°C	ISO 179	31 kJ/m²
Impact strength of simply supported beam without notch		23°C	ISO 179	38 kJ/m²

flammability	Test Condition	Test Method	ASCEND USA/R513H BK
Burning wire flammability index	0.75 mm	IEC 60695-2-12	675 °C
		3.0 mm	IEC 60695-2-12	675 °C
		1.5 mm	IEC 60695-2-12	675 °C
Extreme Oxygen Index		ISO 4589-2	25 %
Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	700 °C
		3.0 mm	IEC 60695-2-13	700 °C
		0.75 mm	IEC 60695-2-13	700 °C
UL flame retardant rating	3.0 mm	UL 94	HB
		0.75 mm	UL 94	HB
		1.5 mm	UL 94	HB

injection	Test Condition	Test Method	ASCEND USA/R513H BK
drying temperature			80 °C
drying time			4.0 hr
Mold temperature			65 to 95 °C
Processing (melt) temperature			285 to 305 °C
Spray nozzle temperature			280 to 310 °C
Suggested maximum material return ratio			25 %
Temperature at the front of the material cylinder			280 to 310 °C
Temperature at the rear of the barrel			280 to 310 °C
Temperature in the middle of the barrel			280 to 310 °C