Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 G30HBK201 KUAZOT SHANGHAI
VOLGAMID®
Automotive sector、Special materials for wat
Glass fiber reinforced、Thermal stability、30% glass fiber reinforce、Enhanced level、Granular
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | KUAZOT SHANGHAI/G30HBK201 |
|---|---|---|---|
| ash content | ISO3451-4 | 30±2 | |
| Moulding shrinkage | ISO294-4 | -- % | |
| Water absorption rate | ISO 62 | -- % | |
| density | ISO 1183 | 1.36 g/cm³ |
| Mechanical properties | Test Condition | Test Method | KUAZOT SHANGHAI/G30HBK201 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 96.0 kJ/m² | |
| Charpy Notched Impact Strength | ISO 179 | 16.1 kJ/m² | |
| tensile strength | ISO527, 50mm/min | 195 Mpa | |
| elongation | 断裂 | ISO527, 50mm/min | -- % |
| bending strength | 4.55 | 267 Mpa | |
| Rockwell hardness | ISO2039/2 | -- | |
| Flexural modulus | 4.55 | 8308 Mpa |
| Thermal performance | Test Condition | Test Method | KUAZOT SHANGHAI/G30HBK201 |
|---|---|---|---|
| UL Vertical Combustion | UL-94 | HB | |
| 1.81Mpa | ISO 75 | 255 °C |