Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A610MX03 TORAY JAPAN
Torelina®
Casters,Electrical applications,sporting goods
High temperature resistan,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A610MX03 |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 5.1 | |
| Volume resistivity | ASTM D257/IEC 60093 | 1014 Ω.cm |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A610MX03 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 230 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 21.5 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 21 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 1 % | |
| Rockwell hardness | ASTM D785 | 123 | |
| tensile strength | ASTM D638/ISO 527 | 140 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | TORAY JAPAN/A610MX03 |
|---|---|---|---|
| characteristic | 高韧性.低氯 | ||
| Color | 黑色 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/A610MX03 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.97 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A610MX03 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | >260 ℃（℉） |
| melting temperature | 278 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 1.8 mm/mm.℃ |