Certificates
PPA HFZ A-4133 L SOLVAY USA
AMODEL®
Shell、Vehicle electronics
Chemical resistance、Low moisture absorption
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SOLVAY USA/HFZ A-4133 L |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ISO 180/1U | 40 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/HFZ A-4133 L |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 12000 Mpa | |
| bending strength | ISO 178 | 255 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.8 % |
| Flexural modulus | ISO 178 | 11000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 180 Mpa |
| Electrical performance | Test Condition | Test Method | SOLVAY USA/HFZ A-4133 L |
|---|---|---|---|
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 0 |
| Dissipation Factor | 60Hz | ASTM D150 | 6E-03 |
| dielectric constant | 60Hz | ASTM D150 | 3.90 |
| Volume resistivity | ASTM D257 | 1E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| Dissipation Factor | 1MHz | ASTM D150 | 0.016 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 1 |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| dielectric constant | 1MHz | ASTM D150 | 3.70 |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SOLVAY USA/HFZ A-4133 L |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 800 °C | |
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| Burning wire flammability index | IEC 60695-2-12 | 800 °C |
| physical property | Test Condition | Test Method | SOLVAY USA/HFZ A-4133 L |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.50 % |
| Water absorption rate | 24hr | ASTM D570 | 0.26 % |
| Shrinkage rate | TD | ASTM D955 | 1.0 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/HFZ A-4133 L |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：150to250°C | ASTME831 | 1.5E-04 cm/cm/°C |
| MD：150to250°C | ASTME831 | 1.4E-05 cm/cm/°C | |
| MD：0to90°C | ASTME831 | 2E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 310 °C |
| Linear coefficient of thermal expansion | TD：0to90°C | ASTME831 | 6.3E-05 cm/cm/°C |
| melting temperature | ISO 3146 | 327 °C |