PA6 BKV30 FN 000000 LANXESS GERMANY
Durethan® 
--
Glass fiber reinforced、Filler: Glass fiber reinf、30%、Filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
Suspended wall beam without notch impact strength-30°CISO 180/1U60 kJ/m²
23°CISO 180/1U75 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU80 kJ/m²
-30°CISO 179/1eU70 kJ/m²
hardnessTest ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
ball-indentation hardnessISO 2039-1210 Mpa
Supplementary InformationTest ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
ISO ShortcutISO 1874PA6.GR.14-100.GF30
filmTest ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
Thin film puncture strength--7ISO 6603-28.00 J
--8ISO 6603-26.00 J
--7ISO 6603-21070 N
--8ISO 6603-2950 N
Electrical performanceTest ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
dielectric strength23°C,3.00mmIEC 60243-140 KV/mm
relative permittivity23°C,1MHzIEC 602504.00
Compared to the Leakage Tracking Index (CTI)ASTM D3638 V
Dissipation Factor23°C,50HzIEC 602505E-03
23°C,1MHzIEC 602500.0150.015
arc resistanceASTM D495-- sec
dielectric constant23°C,50HzIEC 602504.00
dielectric strength23°C,1.00mmIEC 60243-140 KV/mm
dielectric constant23°C,1MHzIEC 602504.00
Compared to the Leakage Tracking Index (CTI)解决方案BIEC 60112 V
解决方案AIEC 60112 V
Volume resistivity23°CIEC 600931E+15 ohms·cm
relative permittivity23°C,100HzIEC 602504.00
Surface ResistivityIEC 600931E+14 ohms
Dissipation Factor23°C,100HzIEC 602505E-03
Mechanical propertiesTest ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
Tensile strain断裂,23°CISO 527-2/53.0 %
Flexural modulus23°CISO 178/A8600 Mpa
bending strength3.5%StrainISO 178/A-- Mpa
tensile strength 断裂,23°CISO 527-2/5180 Mpa
Tensile creep modulus1000hrISO 899-1-- Mpa
bending strength23°CASTM D790280 Mpa
FlexuralStrainatFlexuralStrength6(23°C)4.0 %
Tensile modulus23°CASTM D6389200 Mpa
tensile strength 断裂,23°CASTM D638180 Mpa
Tensile modulus-5°CISO 527-2/19800 Mpa
Tensile creep modulus1hrISO 899-1-- Mpa
bending strength23°CISO 178280 Mpa
Flexural modulus23°CASTM D7908270 Mpa
elongation断裂,23°CASTM D6383.0 %
flammabilityTest ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
Burning Behavior>1.00mmISO 3795passed
UL flame retardant rating3.0mmUL 94HB
3.2mmUL 94HB
0.8mmUL 94HB
1.5mmUL 94HB
Burning wire flammability index2.0mmIEC 60695-2-12600 °C
Limiting Oxygen IndexISO 4589-222 %
UL flame retardant rating1.6mmUL 94HB
physical property Test ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
Shrinkage rateMD:280°C,3.00mm2ISO 25770.16 %
Apparent densityISO 600.70 g/cm³
Water absorption rate平衡,23°C,50%RHISO 622.1 %
Shrinkage rateTD:280°C,3.00mm2ISO 25770.82 %
Water absorption rate饱和,23°CISO 627.0 %
Shrinkage rateMD:120°C,2hr,3.00mm3ISO 25770.030 %
TD:120°C,2hr,3.00mm3ISO 294-40.12 %
Melt volume flow rate260°C/5.0kgISO 113314.0 cm3/10min
Thermal performanceTest ConditionTest MethodLANXESS GERMANY/BKV30 FN 000000
Heat distortion temperature0.45MPa,未退火,4.00mm，HDTASTM D648215 °C
1.8MPa,未退火,4.00mm，HDTASTM D648200 °C
Linear coefficient of thermal expansionMD：23到55°CISO 11359-22E-05 cm/cm/°C
RTI Imp1.5mmUL 74695.0 °C
Linear coefficient of thermal expansionTD：23to55°CISO 11359-28E-05 cm/cm/°C
RTI Str0.8mmUL 746130 °C
melting temperatureISO 11357-3222 °C
vicat--ISO 306/B120>200 °C
RTI Imp0.8mmUL 74695.0 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/B215 °C
1.8MPa,未退火，HDTISO 75-2/A200 °C
vicat--ISO 306/B50200 °C
RTI Str1.5mmUL 746130 °C
RTI Elec1.5mmUL 746130 °C