TPU NX-95A TAIWAN COATING
--
Bottle cap、Fiber grade、Footwear、parts
high strength、wear resistant、enhance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TAIWAN COATING/NX-95A |
|---|---|---|---|
| Impact strength of simply supported beam gap 11 | 23°C | ISO179/1eA | 5.0 kJ/m² |
| Simply supported beam without notch impact strength 11 | 23°C | ISO179/1eU | 45 kJ/m² |
| Unscented Izod Impact Strength 12 | -30°C | ISO180/1U | 45 kJ/m² |
| Simply supported beam without notch impact strength 11 | -30°C | ISO179/1eU | 45 kJ/m² |
| Impact strength of simply supported beam gap 11 | -30°C | ISO179/1eA | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 80 J/m |
| Suspended wall beam gap impact strength 12 | 23°C | ISO180/1A | 8.0 kJ/m² |
| -30°C | ISO180/1A | 7.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | TAIWAN COATING/NX-95A |
|---|---|---|---|
| Tensile stress | 断裂 | ISO527-2/5 | 125 Mpa |
| Tensile strain 7 | Break | ASTMD638 | 2.7 % |
| Tensile strength 7 | Break | ASTMD638 | 120 Mpa |
| Tensile strain 7 | Yield | ASTMD638 | 2.7 % |
| Bending strength 9,10 | ISO178 | 195 Mpa | |
| Tensile modulus | ISO527-2/1 | 9300 Mpa | |
| Tensile strength 7 | Yield | ASTMD638 | 120 Mpa |
| Flexural Strength8 | Yield,50.0mmSpan | ASTMD790 | 195 Mpa |
| Tensile strain | 屈服 | ISO527-2/5 | 2.0 % |
| Flexural Strength8 | Break,50.0mmSpan | ASTMD790 | 190 Mpa |
| Tensile modulus 6 | ASTMD638 | 9300 Mpa | |
| Bending modulus 9 | ISO178 | 8500 Mpa | |
| 1000Cycles,1000g,CS-17转轮 | ASTMD1044 | 19.0 mg | |
| Bending modulus 8 | 50.0mmSpan | ASTMD790 | 7580 Mpa |
| physical property | Test Condition | Test Method | TAIWAN COATING/NX-95A |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.30to0.80 % |
| TD：--2 | 内部方法 | 0.50to1.0 % | |
| melt mass-flow rate | 250°C/2.16kg | ISO1133 | 17 g/10min |
| Shrinkage rate | TD：--3 | 内部方法 | 0.40to0.60 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.080 % |
| density | ASTMD792 | 1.53 g/cm³ | |
| Water absorption rate | 24hr | ASTMD570 | 0.090 % |
| Shrinkage rate | TD：--5 | 内部方法 | 0.60to0.90 % |
| MD：--2 | 内部方法 | 0.30to0.70 % | |
| MD：--3 | 内部方法 | 0.30to0.50 % | |
| MD：--4 | 内部方法 | 0.50to0.80 % | |
| Specific volume | ASTMD792 | 0.660 cm³/g |