Certificates

PBT 357U-1001 SABIC INNOVATIVE SHANGHAI

VALOX™

Electrical field,Electronic field,Electrical appliances,medicine,Medical supplies,Nursing supplies,Plastic bag,Liquid handling,Lawn equipment,Garden equipment,Non specific food,Outdoor applications,Industrial applications,Household goods,Architectural application field,Lighting applications

Flame retardant,UV resistance,Impact modification

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/357U-1001
Rockwell hardness	R-Scale	ASTM D785	117

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/357U-1001
Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	137 °C
Hot deformation temperature		1.8 MPa, Unannealed, 6.40 mm	ASTM D648	98.0 °C
Linear coefficient of thermal expansion	60 to 138°C，Flow	ASTM E831	1.2E-4 cm/cm/°C
Linear coefficient of thermal expansion		-40 to 40°C，Flow	ASTM E831	9.2E-5 cm/cm/°C
RTI		UL 746	140 °C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/357U-1001
Bending modulus	50.0 mm Span	ASTM D790	2060 Mpa
bending strength	Yield, 50.0 mm Span	ASTM D790	82.0 Mpa
bending strength		Break, 50.0 mm Span	ASTM D790	82.0 Mpa
elongation	Break	ASTM D638	110 %
tensile strength	Yield	ASTM D638	48.0 Mpa
tensile strength		Break	ASTM D638	48.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/357U-1001
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 2
Dielectric constant	1 MHz	ASTM D150	3.20
Dielectric constant		100 Hz	ASTM D150	3.20
Dielectric strength	3.20 mm, in Oil	ASTM D149	19 KV/mm
		1.60 mm, in Oil	ASTM D149	25 KV/mm
		3.20 mm, in Air	ASTM D149	19 KV/mm
Dissipation factor	1 MHz	ASTM D150	0.030
Dissipation factor		100 Hz	ASTM D150	3.0E-3
High arc combustion index		UL 746	PLC 3
High voltage arc tracing rate		UL 746	PLC 3
Hot wire ignition		UL 746	PLC 2
Volume resistivity		ASTM D257	> 1.2E+16 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/357U-1001
Outdoor applicability		UL 746C	f1
Shrinkage rate	Flow : 0.750 to 2.30 mm	Internal Method	0.80 - 1.1 %
		Across FlowFlow : 2.30 to 4.60 mm	Internal Method	1.2 - 1.6 %
		Across FlowFlow : 0.750 to 2.30 mm	Internal Method	0.90 - 1.3 %
		Flow : 2.30 to 4.60 mm	Internal Method	1.0 - 1.4 %
Specific volume		ASTM D792	0.750 cm³/g
Water absorption rate	24 hr	ASTM D570	0.080 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/357U-1001
Dart impact	23°C	ASTM D3029	43.0 43.0 J
Suspended wall beam without notch impact strength	23°C	ASTM D4812	3200 J/m

flammability	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/357U-1001
Extreme Oxygen Index		ASTM D2863	30 %
UL flame retardant rating	0.46 mm	UL 94	HB
		3.0 mm	UL 94	5VA
		0.64 mm	UL 94	V-0

injection	Test Condition	Test Method	SABIC INNOVATIVE SHANGHAI/357U-1001
Back pressure			0.300 to 0.700 Mpa
drying temperature			120 °C
drying time			3.0 to 4.0 hr
Exhaust hole depth			0.025 to 0.038 mm
Mold temperature			50 to 75 °C
Processing (melt) temperature			250 to 265 °C
Screw speed			50 to 100 rpm
Spray nozzle temperature			245 to 260 °C
Suggested injection volume			40 to 80 %
Suggested maximum moisture content			0.020 %
Temperature at the front of the material cylinder			250 to 265 °C
Temperature at the rear of the barrel			240 to 255 °C
Temperature in the middle of the barrel			245 to 260 °C