Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC EXL1132T NA8A005T SABIC INNOVATIVE NANSHA
LEXAN™
Household appliances,Automotive sector,Electronic field,Electrical field
Low temperature resistanc,Easy to process,High mobility,UV resistance
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 65 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 69.6 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 45 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 20 kJ/m² |
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 无断裂 |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 74.0 J |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 55 kJ/m² |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| Rockwell hardness | L 计秤 | ISO 2039-2 | 89 |
| ball-indentation hardness | H358/30 | ISO 2039-1 | 95.0 Mpa |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2150 Mpa | |
| --2 | ASTM D638 | 2260 Mpa | |
| tensile strength | 屈服3 | ASTM D638 | 58.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 120 % |
| 屈服 | ASTM D638 | 5.8 % | |
| 断裂 | ISO 527-2/50 | 120 % | |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 94.0 Mpa |
| --5,6 | ISO 178 | 89.0 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 2240 Mpa |
| tensile strength | 断裂 | ISO 527-2/50 | 56.0 Mpa |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 2320 Mpa |
| tensile strength | 屈服 | ISO 527-2/50 | 57.0 Mpa |
| elongation | 断裂 | ASTM D638 | 110 % |
| 屈服3 | ASTM D638 | 5.7 % | |
| Flexural modulus | ISO 178 | 2240 Mpa | |
| tensile strength | 断裂3 | ASTM D638 | 57.0 Mpa |
| Flexural modulus | --5 | ISO 178 | 2140 Mpa |
| tensile strength | 断裂 | ASTM D638 | 58.7 Mpa |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| Tensile modulus | ASTM D638 | 2280 Mpa | |
| bending strength | 屈服,50.0mm跨距 | ASTM D790 | 95.1 Mpa |
| elongation | 屈服 | ISO 527-2/50 | 5.4 % |
| bending strength | ISO 178 | 85.0 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 58.1 Mpa |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| Tensile modulus | -- | ISO 527-2/1 | 2340 Mpa |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| Volume resistivity | ASTM D257 | > 1.0E+15 ohms·cm | |
| Surface Resistivity | ASTM D257 | > 1.0E+15 ohms |
| optical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| transmissivity | 2540 µm | ASTM D1003 | 82.0 % |
| Haze ratio | 2540 µm | ASTM D1003 | 3.0 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.8 mm | IEC 60695-2-13 | 850 °C |
| 3.0 mm | IEC 60695-2-13 | 850 °C | |
| 3.0mm | IEC 60695-2-13 | 875 °C | |
| 1.0mm | IEC 60695-2-13 | 875 °C | |
| Burning wire flammability index | 3.0 mm | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 850 °C |
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40-0.80 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.090 % |
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % |
| Melt volume flow rate | 300°C/1.2 kg | ISO 1133 | 19.0 cm3/10min |
| 300°C/1.2kg | ISO 1133 | 16.0 cm3/10min | |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.40-0.80 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| 饱和,23°C | ISO 62 | 0.35 % | |
| melt mass-flow rate | 300°C/1.2 kg | ASTM D1238 | 20 g/10 min |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.40 - 0.80 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.12 % |
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 17 g/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| Linear coefficient of thermal expansion | 流动 : -40 到 95°C | ASTM E831 | 7.5E-5 cm/cm/°C |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.6E-5 cm/cm/°C | |
| 流动 : 23 到 80°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| MD：-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C | |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 137 °C |
| vicat | ASTM D152511 | 144 °C | |
| Heat distortion temperature | 1.8MPa,Unannealed,100mmSpan，HDT | ISO 75-2/Ae | 125 °C |
| ball-indentation hardness | 123 到 127°C | IEC 60695-10-2 | 通过 |
| RTI Str | UL 746 | 125 °C | |
| RTI | UL 746 | 130 °C | |
| vicat | -- | ISO 306/B120 | 139 °C |
| -- | ASTM D152510 | 138 °C | |
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 7.6E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,Annealed，HDT | ISO 75-2/Be | 136 °C |
| vicat | -- | ISO 306/B50 | 144 °C |
| Linear coefficient of thermal expansion | MD：23到80°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| RTI Imp | UL 746 | 120 °C | |
| Heat distortion temperature | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距9，HDT | ISO 75-2/Af | 116 °C |
| Linear coefficient of thermal expansion | TD：23to80°C | ISO 11359-2 | 7.5E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 124 °C |
| Linear coefficient of thermal expansion | 横向 : -40 到 95°C | ASTM E831 | 7.6E-5 cm/cm/°C |
| RTI Elec | UL 746 | 130 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| Heat distortion temperature | 1.8 MPa, 未退火, 3.20 mm，HDT | ASTM D648 | 121 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/EXL1132T NA8A005T |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 295 to 315 °C | ||
| drying temperature | 120 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 3.0 to 4.0 hr | ||
| Temperature in the middle of the barrel | 280 to 305 °C | ||
| Temperature at the rear of the barrel | 270 to 295 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 295 to 315 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 70 to 95 °C | ||
| Spray nozzle temperature | 290 to 310 °C |