PC MN-8030Q TEIJIN JAPAN
PANLITE®
Lighting applications、Automotive External Parts
UV resistance、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | TEIJIN JAPAN/MN-8030Q |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | TEIJIN JAPAN/MN-8030Q |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2300 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 62.0 Mpa |
| bending strength | ISO 178 | 92.0 Mpa | |
| Flexural modulus | ISO 178 | 2250 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 110 % |
| 屈服 | ISO 527-2/50 | 4.0 % | |
| tensile strength | 断裂 | ISO 527-2/50 | 56.0 Mpa |
| Electrical performance | Test Condition | Test Method | TEIJIN JAPAN/MN-8030Q |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms |
| physical property | Test Condition | Test Method | TEIJIN JAPAN/MN-8030Q |
|---|---|---|---|
| Melt volume flow rate | 280°C/2.16kg | ISO 1133 | 11.0 cm3/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.22 % |
| Shrinkage rate | MD:4.00mm | 内部方法 | 0.70-1.0 % |
| TD:4.00mm | 内部方法 | 0.70-1.0 % |
| Thermal performance | Test Condition | Test Method | TEIJIN JAPAN/MN-8030Q |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 123 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 104 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-05 cm/cm/°C |
| TD | ISO 11359-2 | 8E-05 cm/cm/°C |