Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM SW-01 JAPAN POLYPLASTIC
DURACON®
Automotive sector
High sliding、wear resistant、currency
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | JAPAN POLYPLASTIC/SW-01 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.4 kJ/m² |
| hardness | Test Condition | Test Method | JAPAN POLYPLASTIC/SW-01 |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 70 |
| Supplementary Information | Test Condition | Test Method | JAPAN POLYPLASTIC/SW-01 |
|---|---|---|---|
| ColorNumber | CF2001/CD3501 |
| Electrical performance | Test Condition | Test Method | JAPAN POLYPLASTIC/SW-01 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 2E+14 ohms·cm | |
| dielectric strength | 3.00mm | IEC 60243-1 | 18 KV/mm |
| Mechanical properties | Test Condition | Test Method | JAPAN POLYPLASTIC/SW-01 |
|---|---|---|---|
| Wear factor | 0.98MPa,0.30m/sec4 | JISK7218 | <1.0 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec7 | JISK7218 | 900 10^-8mm³/N·m | |
| Tensile modulus | ISO 527-2 | 2700 Mpa | |
| Wear factor | 0.98MPa,0.30m/sec5 | JISK7218 | 16 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec6 | JISK7218 | 400 10^-8mm³/N·m | |
| Nominal tensile fracture strain | ISO 527-2 | 20 % | |
| coefficient of friction | 与钢-动态3 | JISK7218 | 0.14 |
| bending strength | ISO 178 | 75.0 Mpa | |
| Flexural modulus | ISO 178 | 2500 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.21 |
| tensile strength | ISO 527-2 | 50.0 Mpa |
| flammability | Test Condition | Test Method | JAPAN POLYPLASTIC/SW-01 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | JAPAN POLYPLASTIC/SW-01 |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 6.00 cm3/10min |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 2.0 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.60 % |
| density | ISO 1183 | 1.42 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 7.0 g/10min |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 1.7 % |
| Thermal performance | Test Condition | Test Method | JAPAN POLYPLASTIC/SW-01 |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：23to55°C | 内部方法 | 1.1E-04 cm/cm/°C |
| MD：23到55°C | 内部方法 | 1.1E-04 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 80.0 °C |