Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PC EXL1132-WH9G700 SABIC INNOVATIVE NANSHA

LEXAN™

Household appliances,Automotive sector,Electronic field,Electrical field

Low temperature resistanc,Easy to process,High mobility,UV resistance

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1132-WH9G700
Ball Pressure Test	H358/30	ISO 2039-1	95.0 Mpa

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1132-WH9G700
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124 °C
		0.45MPa,Annealed	ISO 75-2/Be	136 °C
		0.45MPa,Unannealed,3.20mm	ASTM D648	137 °C
		1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	125 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.2E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	7.6E-05 cm/cm/°C
		TD：23to80°C	ISO 11359-2	7.5E-05 cm/cm/°C
		MD：23to80°C	ISO 11359-2	7.5E-05 cm/cm/°C
RTI Elec		UL 746	130 °C
RTI Imp		UL 746	120 °C
RTI Str		UL 746	125 °C
Vicat softening temperature	--	ISO 306/B120	145 °C
		--	ISO 306/B50	144 °C
			ASTM D152511	144 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1132-WH9G700
Bending modulus	50.0mmSpan	ASTM D790	2320 Mpa
Bending modulus			ISO 178	2240 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	95.1 Mpa
bending strength			ISO 178	85.0 Mpa
elongation	Break	ASTM D638	110 %
elongation		Yield	ASTM D638	5.8 %
Tensile modulus		ASTM D638	2280 Mpa
Tensile modulus			ISO 527-2/1	2150 Mpa
Tensile strain	Break	ISO 527-2/50	100 %
Tensile strain		Yield	ISO 527-2/50	5.0 %
tensile strength	Yield	ASTM D638	58.1 Mpa
		Yield	ISO 527-2/50	57.0 Mpa
		Break	ISO 527-2/50	55.0 Mpa
		Break	ASTM D638	58.7 Mpa

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1132-WH9G700
melt mass-flow rate	300°C/1.2kg	ASTM D1238	17 g/10min
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	16.0 cm3/10min
Shrinkage rate	TD：3.20mm	Internal Method	0.40-0.80 %
Shrinkage rate		MD：3.20mm	Internal Method	0.40-0.80 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate		Saturation,23°C	ISO 62	0.35 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1132-WH9G700
Charpy Notched Impact Strength	23°C	ISO 179/1eA	60 kJ/m²
Charpy Notched Impact Strength		-30°C	ISO 179/1eA	25 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	69.6 J
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	20 kJ/m²
Impact strength of cantilever beam gap		23°C	ISO 180/1A	55 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	NoBreak

flammability	Test Condition	Test Method	SABIC INNOVATIVE NANSHA/EXL1132-WH9G700
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
Burning wire flammability index		1.0mm	IEC 60695-2-12	850 °C
Extreme Oxygen Index		ISO 4589-2	32 %
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	875 °C
Hot filament ignition temperature		1.0mm	IEC 60695-2-13	875 °C