Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 A3X2G5 BASF GERMANY
Ultramid®
Electrical applications,Electrical components
Electrical performance,Flame retardant,Oil resistant
UL
SGS
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | BASF GERMANY/A3X2G5 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 10^13/10^10 Ω | |
| dielectric constant | 1MHz，干/湿 | 3.7/5 | |
| Compared to the Leakage Traceability Index (CTI) | 干/湿 | CTI 500 | |
| dielectric strength | K20/P50，干/湿 | 80/65 KV/mm | |
| Surface Resistivity | 干/湿 | >10 Ω | |
| loss angle | 1MHz，干/湿 | 0.02/0.1 | |
| Volume resistivity | ASTM D257/IEC 60093 | 10^15/10^12 Ω.cm | |
| 干/湿 | 10 Ω.cm |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/A3X2G5 |
|---|---|---|---|
| Tensile creep modulus | 1000h,湿 | 3500 Mpa | |
| Charpy Notched Impact Strength | +23℃，干/湿 | 65/70 KJ/m | |
| Fracture stress (V=50mm/min) | 干/湿 | 140/100 Mpa | |
| Charpy Notched Impact Strength | 30℃，干 | 60 KJ/m | |
| Flexural modulus | 干/湿 | 7100 Mpa | |
| elongation | ≤0.5%, +23℃，湿 | 3500 Mpa | |
| ball-indentation hardness | 干/湿 | 190 Mpa | |
| elongation at break | ASTM D638/ISO 527 | 3/4.5 % | |
| tensile strength | ASTM D638/ISO 527 | 140/100 kg/cm²(MPa)[Lb/in²] | |
| Tensile yield stress (V=50mm/min) | 干/湿 | 140/100 Mpa | |
| Impact Strength | +23℃，干/湿 | 4/10 J | |
| Tensile modulus | 干/湿 | 8500/6000 Mpa | |
| Impact strength of cantilever beam gap | +23℃，干/湿 | 11/17 KJ/m | |
| Tensile modulus | ASTM D638/ISO 527 | 8500/6000 kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | - kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | 干/湿，V=50mm/min | 3/4.5 % |
| other | Test Condition | Test Method | BASF GERMANY/A3X2G5 |
|---|---|---|---|
| characteristic | 玻纤增强注射级.红磷阻燃剂长期稳定性.具有优异的机械性能和电性能 |
| Physical properties | Test Condition | Test Method | BASF GERMANY/A3X2G5 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.34 | |
| Water absorption rate | ASTM D570/ISO 62 | 5.7-6.3 % |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/A3X2G5 |
|---|---|---|---|
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 250 1.8Mpa ℃（℉） |
| TEMPERATURE | 在20000h/5000h，后拉伸强度下降50%时 | 139/157 °C | |
| Heat distortion temperature | 1.8MPa负荷，干态，HDT | 250 °C | |
| thermal conductivity | 干态 | 0.27 W/(m.K) | |
| melting temperature | 260 ℃（℉） | ||
| Heat distortion temperature | 0.45MPa负荷，干态，HDT | 250 °C | |
| maximum service temperature | 220 °C | ||
| Linear coefficient of thermal expansion | （23-80）℃，干态 | 2.5-3.5/6-8 | |
| ASTM D696/ISO 11359 | 2.5-3.5/6-8 mm/mm.℃ | ||
| specific heat | 干态 | 1.5 J/(g.K) |