Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM AT342 OTSUKAC JAPAN
POTICON
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | OTSUKAC JAPAN/AT342 |
|---|---|---|---|
| Rockwell hardness | M 级 | ASTM D785 | 74 |
| Mechanical properties | Test Condition | Test Method | OTSUKAC JAPAN/AT342 |
|---|---|---|---|
| Wear amount | -- 3 | 1.30 10^-3 mm³/N·km | |
| elongation | 断裂 | ASTM D638 | 3.3 % |
| 与钢 - 动态 | 0.20 | ||
| bending strength | ASTM D790 | 121 Mpa | |
| tensile strength | ASTM D638 | 82.0 Mpa | |
| Wear amount | of counterpart 4 | 0.00 10^-3 mm³/N·km | |
| Flexural modulus | ASTM D790 | 6100 Mpa |
| flammability | Test Condition | Test Method | OTSUKAC JAPAN/AT342 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | OTSUKAC JAPAN/AT342 |
|---|---|---|---|
| Shrinkage rate | 横向流动 | 1.9 % | |
| Water absorption rate | 平衡 | ASTM D570 | 0.20 % |
| Shrinkage rate | 流动 | 1.2 % |
| Thermal performance | Test Condition | Test Method | OTSUKAC JAPAN/AT342 |
|---|---|---|---|
| ASTM D696 | 3.8E-5 cm/cm/°C | ||
| Heat Distortion | ASTM D648 | 147 °C |
| injection | Test Condition | Test Method | OTSUKAC JAPAN/AT342 |
|---|---|---|---|
| Temperature | 60 到 100 °C | ||
| Processing (melt) temperature | 185 到 215 °C | ||
| Injection Pressure | 70.0 到 100 Mpa |