Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DS-3002R 7041A MITSUBISHI ENGINEERING JAPAN
IUPILON™ 
Casters
Thermal stability,High crystallinity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/DS-3002R 7041A
Impact strength of simply supported beam without notch23°CISO 179NoBreak
Mechanical propertiesTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/DS-3002R 7041A
Tensile modulusISO 527-22500 Mpa
Nominal tensile fracture strainISO 527-2100 %
bending strengthISO 17889.0 Mpa
Flexural modulusISO 1782300 Mpa
Tensile strain屈服ISO 527-26.5 %
tensile strength 屈服ISO 527-259.0 Mpa
Electrical performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/DS-3002R 7041A
Volume resistivityIEC 600933E+16 ohms·cm
Surface ResistivityIEC 600936E+15 ohms
Compared to the Leakage Tracking Index (CTI)CTIUL 746PLC 2
flammabilityTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/DS-3002R 7041A
UL flame retardant rating0.40mmUL 94V-2
physical property Test ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/DS-3002R 7041A
Shrinkage rateTD:3.20mm0.50-0.70 %
Melt volume flow rate300°C/1.2kgISO 113314.0 cm3/10min
Shrinkage rate吸水率(饱和,23°C)0.24 %
MD:3.20mm0.50-0.70 %
melt mass-flow rate300°C/1.2kgISO 113314 g/10min
Thermal performanceTest ConditionTest MethodMITSUBISHI ENGINEERING JAPAN/DS-3002R 7041A
Heat distortion temperature0.45MPa,未退火,HDTISO 75-2/B134 °C
1.8MPa,未退火,HDTISO 75-2/A121 °C
Linear coefficient of thermal expansionMDISO 11359-26.5E-05 cm/cm/°C
TDISO 11359-26.6E-05 cm/cm/°C