EHMWPE Quadrant EPP TIVAR® SuperPlus Mitsubishi Chemical Advanced Materials
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Test Condition | Test Method | Mitsubishi Chemical Advanced Materials/Quadrant EPP TIVAR® SuperPlus | |
---|---|---|---|
coefficient of friction | 与钢-静态 | 内部方法 | 0.15 |
Water absorption rate | 饱和 | ASTM D570 | <0.010 % |
UL flame retardant rating | 3.2mm | UL 94 | HB |
elongation | 断裂 | ASTM D638 | 300 % |
Tensile modulus | ASTM D638 | 703 MPa | |
Shore hardness | 邵氏D | ASTM D2240 | 70 |
dielectric strength | ASTM D149 | 91 kV/mm | |
bending strength | 屈服 | ASTM D790 | 21.4 MPa |
Linear coefficient of thermal expansion | MD2:-40到149°C | ASTME831 | 2.2E-04 cm/cm/°C |
tensile strength | 极限 | ASTM D638 | 36.5 MPa |
density | ASTM D792 | 0.960 g/cm³ | |
thermal conductivity | 0.41 W/m/K | ||
Dissipation Factor | 1MHz | ASTM D150 | 5E-04 |
Flexural modulus | ASTM D790 | 586 MPa | |
dielectric constant | 1MHz | ASTM D150 | 2.30 |
Water absorption rate | 24hr | ASTM D570 | <0.010 % |
Compression Modulus | ASTM D695 | 414 MPa | |
Heat distortion temperature | 1.8MPa,未退火,HDT | ASTM D648 | 46.7 °C |
Maximum operating temperature LongTerm, Air | 104 °C | ||
Crystallization peak temperature | DSC | ASTM D3418 | 135 °C |
Surface Resistivity | ASTM D257 | >1.0E+15 ohms | |
limiting pv value | 内部方法 | 0.0701 MPa·m/s | |
compressive strength | 10%应变,23°C | ASTM D695 | 20.7 MPa |
Impact strength of cantilever beam gap | ASTM D256A | 无断裂 |