PBT/PET PCR GF 45 BK A SCHULMAN USA
SCHULADUR®
--
Filler: Glass fiber reinf、45% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | A SCHULMAN USA/PCR GF 45 BK |
---|---|---|---|
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 50 kJ/m² |
-30°C | ISO 179/1eU | 50 kJ/m² |
Mechanical properties | Test Condition | Test Method | A SCHULMAN USA/PCR GF 45 BK |
---|---|---|---|
Tensile modulus | ISO 527-2/1A/1 | 15500 Mpa | |
bending strength | ISO 178 | 250 Mpa | |
Flexural modulus | ISO 178 | 16000 Mpa | |
tensile strength | 断裂 | ISO 527-2/1A/5 | 160 Mpa |
Tensile strain | 断裂 | ISO 527-2/1A/5 | 1.7 % |
flammability | Test Condition | Test Method | A SCHULMAN USA/PCR GF 45 BK |
---|---|---|---|
Burning wire flammability index | 3.0mm | IEC 60695-2-12 | 800 °C |
UL flame retardant rating | 1.6mm | IEC 60695-11-10,-20 | HB |
3.2mm | IEC 60695-11-10,-20 | HB | |
Burning wire flammability index | 1.5mm | IEC 60695-2-12 | 700 °C |
Hot filament ignition temperature | 3.0mm,Passes | IEC 60695-2-13 | 800 °C |
burning rate | ISO 3795 | 25 mm/min | |
Hot filament ignition temperature | 1.5mm,Passes | IEC 60695-2-13 | 825 °C |
physical property | Test Condition | Test Method | A SCHULMAN USA/PCR GF 45 BK |
---|---|---|---|
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.25 % |
Melt volume flow rate | 260°C/2.16kg | ISO 1133 | 11.0 cm3/10min |
Thermal performance | Test Condition | Test Method | A SCHULMAN USA/PCR GF 45 BK |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/Af | 208 °C |
vicat | -- | ISO 306/A50 | 214 °C |
-- | ISO 306/B50 | 198 °C | |
Heat distortion temperature | 0.45MPa,未退火,HDT | ISO 75-2/Bf | 225 °C |