Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC KG-20MRA KOTEC JAPAN
CARBO TEX
--
Fiber grade、Glass fiber reinforced、Filler: Glass fiber reinf、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| Water absorption rate | 23 ℃ | ASTM D-570 | 0.11 % |
| Mechanical properties | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 85 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | V-缺口，3.2mm | ASTM D-256 | 10-14 kJ/m² |
| bending strength | ASTM D790 | 152 Mpa | |
| ASTM D-790 | 5680 Mpa | ||
| Flexural modulus | ASTM D-790 | 98-137 J/m | |
| tensile strength | 断裂 | ASTM D638 | 108 Mpa |
| ASTM D-638 | 108 Mpa | ||
| elongation at break | ASTM D638/ISO 527 | 4.0 % | |
| tensile strength | ASTM D638/ISO 527 | 640 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790 | 5690 Mpa | |
| elongation | 断裂 | ASTM D-638 | 4 % |
| 断裂 | ASTM D638 | 4.0 % | |
| Rockwell hardness | ASTM D-785 | 121 |
| Electrical performance | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+16 ohms·cm | |
| ASTM D-25 | 1014 Ω.cm | ||
| Dissipation Factor | 1MHz | ASTM D150 | 8E-03 |
| dielectric constant | 10HZ | ASTM D-150 | 3.3 |
| 1MHz | ASTM D150 | 3.20 | |
| arc resistance | ASTM D-495 | 110 sec | |
| dielectric strength | 1.60mm | ASTM D149 | 20 KV/mm |
| Volume resistivity | ASTM D257/IEC 60093 | 10^16 Ω.cm | |
| arc resistance | ASTM D495 | 110 sec |
| other | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| characteristic | 低粘度.高流量.易脱模品级 | ||
| Color | 透明 | ||
| purpose | 注塑.薄成型. |
| optical performance | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| Haze ratio | 3.00mm | ASTM D1003 | Translucent |
| Physical properties | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.30 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 15 g/10min |
| flammability | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.30-0.50 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | <0.20 % |
| Thermal performance | Test Condition | Test Method | KOTEC JAPAN/KG-20MRA |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-2/1.6mm | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 145 °C |
| HDT | ASTM D-648 | 140-148 °C | |
| HDT | ASTM D648/ISO 75 | 133 ℃（℉） |