PC EXL6411 GY6D093 SABIC INNOVATIVE JAPAN
LEXAN™
Electronic and Electrical、Aerospace Applications、lens
High mobility、Ductility at low temperat、Short molding cycle
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/EXL6411 GY6D093 |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 70 kJ/m² |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
Suspended wall beam without notch impact strength | -30°C9 | ISO 180/1U | 无断裂 |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 62.1 J |
-30°C,TotalEnergy | ASTM D3763 | 61.0 J | |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 60 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 3200 J/m |
23°C9 | ISO 180/1U | 无断裂 |
Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/EXL6411 GY6D093 |
---|---|---|---|
High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 3 |
Volume resistivity | IEC 60093 | 1.7E+17 ohms·cm | |
High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
Hot wire ignition (HWI) | HWI | UL 746 | PLC 2 |
dielectric strength | 3.20mm,在油中 | IEC 60243-1 | 18 KV/mm |
arc resistance | ASTM D495 | PLC 5 | |
relative permittivity | 1MHz | IEC 60250 | 2.69 |
Surface Resistivity | IEC 60093 | 4.1E+17 ohms | |
Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 3 |
Dissipation Factor | 1MHz | IEC 60250 | 9.4E-03 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/EXL6411 GY6D093 |
---|---|---|---|
bending strength | 屈服,50.0mm跨距5 | ASTM D790 | 79.3 Mpa |
tensile strength | 屈服4 | ASTM D638 | 55.2 Mpa |
elongation | 断裂4 | ASTM D638 | 100 % |
Tensile modulus | --3 | ASTM D638 | 1720 Mpa |
elongation | 断裂 | ISO 527-2/50 | 88 % |
Flexural modulus | 50.0mm跨距5 | ASTM D790 | 2000 Mpa |
bending strength | --6,7 | ISO 178 | 85.0 Mpa |
Flexural modulus | --6 | ISO 178 | 2090 Mpa |
tensile strength | 断裂 | ISO 527-2/50 | 58.0 Mpa |
屈服 | ISO 527-2/50 | 54.0 Mpa | |
elongation | 屈服 | ISO 527-2/50 | 6.0 % |
屈服4 | ASTM D638 | 5.5 % | |
tensile strength | 断裂4 | ASTM D638 | 60.0 Mpa |
Tensile modulus | -- | ISO 527-2/1 | 2280 Mpa |
flammability | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/EXL6411 GY6D093 |
---|---|---|---|
UL flame retardant rating | 1.5mm | UL 94 | HB |
physical property | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/EXL6411 GY6D093 |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.40-0.80 % |
Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 7.50 cm3/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
饱和,23°C | ISO 62 | 0.35 % | |
Shrinkage rate | TD:3.20mm | 内部方法 | 0.40-0.80 % |
melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 8.0 g/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE JAPAN/EXL6411 GY6D093 |
---|---|---|---|
Linear coefficient of thermal expansion | TD:23到80°C | ISO 11359-2 | 7.3E-05 cm/cm/°C |
Heat distortion temperature | 0.45MPa,未退火,100mm跨距10,HDT | ISO 75-2/Be | 136 °C |
0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 136 °C | |
1.8MPa,未退火,100mm跨距10,HDT | ISO 75-2/Ae | 122 °C | |
Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 6.9E-05 cm/cm/°C |
RTI | UL 746 | 80.0 °C | |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
vicat | -- | ISO 306/B120 | 140 °C |
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7.2E-05 cm/cm/°C |
RTI Imp | UL 746 | 80.0 °C | |
vicat | -- | ASTMD152511 | 141 °C |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 122 °C |
ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
RTI Elec | UL 746 | 80.0 °C |