PC XHT4141-GY8D046 SABIC INNOVATIVE US
LEXAN™ 
Casters、Sports Equipment
High mobility、transparent、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Thermal PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
RTIUL 746150 °C
Linear thermal expansion coefficient横向 : -40 到 40°CASTM E8316.0E-5 cm/cm/°C
Ball PressureTest163 到 167°CIEC 60695-10-2通过
Vicat Softening Temperature--ISO 306/B120181 °C
RTI ElecUL 746150 °C
Thermal Conductivity25°CASTM C1770.20 W/m/K
Linear thermal expansion coefficient流动 : -40 到 40°CASTM E831, ISO 11359-26.0E-5 cm/cm/°C
Deflection Temperature Under Load?0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9ISO 75-2/Bf173 °C
Linear thermal expansion coefficient横向 : -40°CISO 11359-26.0E-5 cm/cm/°C
Ball PressureTest123 到 127°CIEC 60695-10-2通过
Deflection Temperature Under Load?1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 9ISO 75-2/Af162 °C
RTI ImpUL 746130 °C
Deflection Temperature Under Load?1.8 MPa, 未退火, 3.20 mmASTM D648165 °C
Vicat Softening Temperature--ASTM D152510, ISO 306/B5010183 °C
Deflection Temperature Under Load?0.45 MPa, 未退火, 3.20 mmASTM D648174 °C
InjectionTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Middle Temperature290 到 335 °C
Drying Time4.0 到 6.0 hr
Suggested Shot Size40 到 60 %
Drying Temperature135 °C
Mold Temperature95 到 130 °C
Vent Depth0.025 到 0.080 mm
Suggested Max Moisture0.020 %
Processing (Melt) Temp300 到 345 °C
Rear Temperature280 到 325 °C
Nozzle Temperature295 到 340 °C
Front Temperature300 到 345 °C
Back Pressure0.300 到 0.700 Mpa
Screw Speed40 到 90 rpm
PhysicalTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Moisture Absorption平衡, 23°C, 50% RHISO 620.25 %
Melt Mass-Flow Rate330°C/2.16 kgASTM D123825 g/10 min
Melt Volume flow Rate330°C/2.16 kgISO 113324.0 cm3/10min
Modeling Shrinkage - Flow3.20 mm内部方法0.60 到 0.95 %
Moisture Absorption饱和, 23°CISO 620.50 %
Mechanical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Tensile Strength断裂ISO 527-2/5067.0 Mpa
Tensile Modulus--ISO 527-2/12750 Mpa
Tensile Elongation断裂 3ASTM D63850 %
Tensile Strength屈服 3ASTM D63877.0 Mpa
Tensile Elongation屈服ISO 527-2/507.0 %
Flexural Modulus50.0 mm 跨距 4ASTM D7902600 Mpa
Tensile Modulus-- 2ASTM D6382730 Mpa
Tensile Strength屈服ISO 527-2/5078.0 Mpa
Flexural Stress屈服, 50.0 mm 跨距 4ASTM D790120 Mpa
Tensile Elongation屈服 3ASTM D6387.0 %
Flexural Stress-- 5, 6ISO 17880.0 Mpa
Flexural Modulus-- 5ISO 1782600 Mpa
Tensile Elongation断裂ISO 527-2/5050 %
Tensile Strength断裂 3ASTM D63869.0 Mpa
Impact PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Unnotched Izod Impact Strength23°CISO 180/1U无断裂
Instrumented Dart Impact23°C, Total EnergyASTM D376372.0 J
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
23°CISO 179/1eA11 kJ/m²
Charpy Unnotched Impact Strength23°CISO 179/1eU无断裂
Unnotched Izod Impact Strength-30°CISO 180/1U无断裂
Charpy Unnotched Impact Strength-30°CISO 179/1eU无断裂
FlammabilityTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
内部方法175 °C
UL flame retardant rating3.0 mmUL 94HB
Glow Wire Flammability Index3.0 mmIEC 60695-2-12960 °C
Glow Wire Ignition Temperature3.0 mmIEC 60695-2-13875 °C
UL flame retardant rating1.5 mmUL 94HB
Electrical PropertiesTest ConditionTest MethodSABIC INNOVATIVE US/XHT4141-GY8D046
Volume ResistivityASTM D257> 1.0E+17 ohms·cm
Hot-wire IgnitionUL 746PLC 3
Dielectric Constant1 MHzASTM D1503.02
Surface ResistivityASTM D257> 1.0E+17 ohms
High Amp Arc IgnitionUL 746PLC 0
Dielectric Constant100 HzASTM D1503.12