Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 PX11311U WHPF059 SABIC INNOVATIVE MEXICO
LNP™ KONDUIT™ Compound
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/PX11311U WHPF059 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 25 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 3.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/PX11311U WHPF059 |
|---|---|---|---|
| dielectric strength | 1.60mm,inOil | ASTM D149 | 16 KV/mm |
| Surface Resistivity | ASTM D257 | 1E+16 ohms | |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 0 |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| IEC 60112 | V |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/PX11311U WHPF059 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 12000 Mpa | |
| tensile strength | 断裂 | ISO 527-2/5 | 105 Mpa |
| bending strength | ISO 178 | 170 Mpa | |
| Flexural modulus | ISO 178 | 11000 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 1.7 % |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/PX11311U WHPF059 |
|---|---|---|---|
| Hot filament ignition temperature | 1.50mm | IEC 60695-2-13 | 775 °C |
| UL flame retardant rating | 1.00mm | UL 94 | V-0V-0 |
| Hot filament ignition temperature | 3.00mm | IEC 60695-2-13 | 800 °C |
| 1.00mm | IEC 60695-2-13 | 800 °C | |
| Burning wire flammability index | 1.00mm | IEC 60695-2-12 | 960 °C |
| Hot filament ignition temperature | 1.60mm | IEC 60695-2-13 | 775775 °C |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/PX11311U WHPF059 |
|---|---|---|---|
| Shrinkage rate | MD:24小时 | ISO 294-4 | 0.45 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.36 % |
| Shrinkage rate | TD:24小时 | ISO 294-4 | 0.65 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE MEXICO/PX11311U WHPF059 |
|---|---|---|---|
| Horizontal: 23 to 80 ° C | 横向, 23到80℃ | ISO 11359-2 | 7.3E-05 cm/cm/°C |
| Flow: -30 to 80 ° C | ISO 11359-2 | 3.5E-05 cm/cm/°C | |
| Flow: -40 to 40 ° C | ASTME831 | 3.1E-53.1E-5 cm/cm/°C | |
| Horizontal: -30 to 80 ° C | ISO 11359-2 | 6E-05 cm/cm/°C | |
| 0.45MPa, Unanealed, 3.20mm | ASTM D648 | 209 °C | |
| thermal conductivity | --7 | ISO 22007-2 | 0.80 W/m/K |
| Flow: 23 to 80 ° C | 23到80℃ | ISO 11359-2 | 3.7E-05 cm/cm/°C |
| thermal conductivity | --8 | ISO 22007-2 | 1.11.1 W/m/K |
| vicat | ISO 306/B120 | 205 °C | |
| thermal conductivity | --9 | ISO 22007-2 | 1.31.3 W/m/K |
| --10 | ISO 22007-2 | 1.5 W/m/K | |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | Pass |
| Horizontal: -40 to 40 ° C | 横向, -40到40℃ | ASTME831 | 4.8E-54.8E-5 cm/cm/°C |
| 0.45MPa, Unanealed, 64.0mm span | ISO 75-2/Bf | 208 °C | |
| 1.8MPa, Unanealed, 64.0mm span | ISO 75-2/Af | 185 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | PassPass |