POM HC750 ASAHI JAPAN
TENAC™-C
Automotive sector、Electrical field、Electronic field、Household goods、Industrial applications
copolymer、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Basic performance | Test Condition | Test Method | ASAHI JAPAN/HC750 |
|---|---|---|---|
| Water absorption rate | 24 hr | ASTM D570 | 0.2 % |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/HC750 |
|---|---|---|---|
| Tensile stress | 屈服 | ISO 527-2 | 71 MPa |
| Tensile modulus | ISO 527-2 | 3200 MPa | |
| ASTM D638/ISO 527 | 3200(MPa) kg/cm²(MPa)[Lb/in²] | ||
| bending strength | ASTM D790 | 98 MPa | |
| Impact strength of cantilever beam gap | ASTM D256 | 59 J/m | |
| elongation | 断裂 | ISO 527-2 | 45 % |
| Physical properties | Test Condition | Test Method | ASAHI JAPAN/HC750 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 1.6-2.0 % | |
| density | ASTM D792/ISO 1183 | 1.41 |
| physical property | Test Condition | Test Method | ASAHI JAPAN/HC750 |
|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 1.6-2 % |
| Flow | ASTM D955 | 1.6-2 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/HC750 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 1.8MPa,unannealed，HDT | ASTM D648 | 124 ℃ |
| 0.45MPa,unannealed，HDT | ASTM D648 | 163 ℃ | |
| 1.8MPa,unannealed，HDT | ISO 75-2/A | 107 ℃ | |
| UL flame retardant rating | UL 94 | HB |