Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PET FR543 BK507 DUPONT KOREA
Rynite®
Automotive Applications、household electrical appl
Glass fiber reinforced、High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT KOREA/FR543 BK507 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23℃ | ISO 179 | 10.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | DUPONT KOREA/FR543 BK507 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 1.5 % |
| tensile strength | 断裂 | ISO 527 | 155 Mpa |
| bending strength | ISO 178 | 275 Mpa | |
| Flexural modulus | ISO 178 | 16500 Mpa | |
| elongation | 断裂 | ISO 527 | 1.6 % |
| Poisson's ratio | ISO 527 | 0.33 | |
| Tensile modulus | ISO 527 | 15600 Mpa | |
| tensile strength | ASTM D638 | 160 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT KOREA/FR543 BK507 |
|---|---|---|---|
| RTI Imp | 本色 黑色 1.5 mm | UL 746B | 155 °C |
| RTI Str | 本色 黑色 3.0 mm | UL 746B | 155 °C |
| Volume resistivity | ASTM D257 | 100000000000000 ohms·cm | |
| High arc combustion index (HAI) | 本色 黑色 3.0 mm | UL 746A | PLC 1 |
| RTI Elec | 本色 黑色 1.5 mm | UL 746B | 155 °C |
| RTI Imp | 本色 黑色 3.0 mm | UL 746B | 155 °C |
| High Voltage Arc Traceability Rate (HVTR) | UL 746A | PLC 0 | |
| High arc combustion index (HAI) | 本色 黑色 1.5 mm | UL 746A | PLC 1 |
| RTI Str | 本色 黑色 0.81 mm | UL 746B | 155 °C |
| dielectric strength | ASTM D149 | 32 KV/mm | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 3 | |
| RTI Imp | 本色 黑色 0.81 mm | UL 746B | 155 °C |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 5 | |
| RTI Elec | 本色 黑色 0.81 mm | UL 746B | 155 °C |
| High arc combustion index (HAI) | 本色 黑色 0.81 mm | UL 746A | PLC 1 |
| arc resistance | ASTM D495 | PLC_5 | |
| RTI Elec | 本色 黑色 3.0 mm | UL 746B | 155 °C |
| RTI Str | 本色 黑色 1.5 mm | UL 746B | 155 °C |
| Flame retardant performance | Test Condition | Test Method | DUPONT KOREA/FR543 BK507 |
|---|---|---|---|
| UL flame retardant rating | 0.81 mm | UL 94 | V-0 |
| burning rate | ISO 3795 | 80 mm/min | |
| GWIT | ISO 11359-2 | 960 °C | |
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 5VA |
| Relative temperature of heating wire | ISO 11359-2 | 960 °C | |
| UL flame retardant rating | 3.0 mm | UL 94 | V-0 5VA |
| physical property | Test Condition | Test Method | DUPONT KOREA/FR543 BK507 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294 | 0.8 % |
| Water absorption rate | ISO 62 | 0.1 % | |
| Shrinkage rate | TD | ISO 294 | 0.2 % |
| melt viscosity | 250°C，1000sˉ¹ | ISO 11443 | 200 Pa·s |
| Thermal performance | Test Condition | Test Method | DUPONT KOREA/FR543 BK507 |
|---|---|---|---|
| melting temperature | ISO 11357 | 254 °C |