Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS GP22 Q552 INEOS STYRO KOREA
Terluran®
small home appliances、Communication plastic par、Electronic communication
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | INEOS STYRO KOREA/GP22 Q552 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 300 J/m |
| -30°C | ISO180/A | 8.0 kJ/m² | |
| 23°C | ISO180/A | 26 kJ/m² | |
| Charpy Notched Impact Strength | -30°C | ISO179 | 8.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 180 kJ/m² |
| Impact strength of cantilever beam gap | -18°C | ASTMD256 | 100 J/m |
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 100 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 59 J/m |
| Charpy Notched Impact Strength | 23°C | ISO179 | 22 kJ/m² |
| hardness | Test Condition | Test Method | INEOS STYRO KOREA/GP22 Q552 |
|---|---|---|---|
| ISO2039-1 | 97.0 Mpa | ||
| Rockwell hardness | R级 | ASTMD785 | 103 |
| Mechanical properties | Test Condition | Test Method | INEOS STYRO KOREA/GP22 Q552 |
|---|---|---|---|
| elongation | 断裂 | ASTMD638 | 2.6 % |
| Flexural modulus | ASTMD790 | 2300 Mpa | |
| Tensile strain | 屈服,23°C | ISO527-2 | 2.6 % |
| Nominal tensile fracture strain | 23°C | ISO527-2 | 10 % |
| tensile strength | 屈服,23°C | ASTMD638 | 45.0 Mpa |
| Bending stress | ISO178 | 65.0 Mpa | |
| Tensile modulus | ISO527-2 | 2300 Mpa | |
| ASTMD638 | 2300 Mpa | ||
| Tensile stress | 屈服,23°C | ISO527-2 | 45.0 Mpa |
| bending strength | ASTMD790 | 65.0 Mpa |
| Electrical performance | Test Condition | Test Method | INEOS STYRO KOREA/GP22 Q552 |
|---|---|---|---|
| Surface Resistivity | IEC60093 | 1E+13 ohms | |
| Dissipation Factor | 1MHz | IEC60250 | 7.9E-03 |
| Volume resistivity | ASTMD257 | >1.0E+15 ohms·cm | |
| 1MHz | IEC60250 | 2.80 | |
| Volume resistivity | IEC60093 | 1E+15 ohms·cm | |
| dielectric constant | 1.00mm,1MHz | ASTMD150 | 2.80 |
| 100Hz | IEC60250 | 2.90 | |
| Dissipation Factor | 100Hz | IEC60250 | 4.8E-03 |
| optical performance | Test Condition | Test Method | INEOS STYRO KOREA/GP22 Q552 |
|---|---|---|---|
| Yellowness Index | DIN6167 | 13 YI |
| physical property | Test Condition | Test Method | INEOS STYRO KOREA/GP22 Q552 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.22 % |
| melt mass-flow rate | 200°C/5.0kg | ASTMD1238 | 1.5 g/10min |
| Water absorption rate | 饱和,23°C | ISO62 | 1.0 % |
| density | ASTMD792 | 1.04 g/cm³ | |
| Shrinkage rate | MD | ASTMD955 | 0.40to0.70 % |
| Melt volume flow rate | 230°C/3.8kg | ASTMD1238 | 4.80 cm3/10min |
| density | ISO1183 | 1.04 g/cm³ | |
| melt mass-flow rate | 220°C/10.0kg | ASTMD1238 | 19 g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 19.0 cm3/10min |
| Shrinkage rate | ISO294-4 | 0.40to0.70 % | |
| Water absorption rate | 饱和,23°C | ASTMD570 | 1.0 % |
| Thermal performance | Test Condition | Test Method | INEOS STYRO KOREA/GP22 Q552 |
|---|---|---|---|
| thermal conductivity | DIN52612 | 0.17 W/m/K | |
| 0.45MPa,未退火 | ASTMD648 | 90.6 °C | |
| vicat | -- | ISO306/A50 | 105 °C |
| MD | ISO11359-2 | 8.0E-5to1.1E-4 cm/cm/°C | |
| 1.8MPa,退火 | ISO75-2/A | 94.0 °C | |
| 0.45MPa,Annealed | ISO75-2/B | 99.0 °C | |
| vicat | -- | ISO306/B50 | 96.0 °C |
| 0.45MPa,退火 | ASTMD648 | 104 °C | |
| 1.8MPa,未退火 | ASTMD648 | 77.8 °C | |
| 1.8MPa,退火 | ASTMD648 | 98.9 °C |