PBT 5010G-30 MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Bottle cap,Fitness equipment,Automotive sector,Electronic field,Electrical field
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.E+15 Ω | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.E+14 Ω.cm |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 210 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 8900 kg/cm²(MPa)[Lb/in²] | |
| Tensile modulus | ASTM D638/ISO 527 | 9500 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 |
|---|---|---|---|
| purpose | 30%玻纤增强 |
| Physical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.2 % | |
| density | ASTM D792/ISO 1183 | 1.52 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 15 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.07 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/5010G-30 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 220 ℃（℉） |
| melting temperature | 224 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 3.E-05 mm/mm.℃ |