Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEN NOPLA® KE901 KOLON KOREA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | KOLON KOREA/NOPLA® KE901 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 3.0 kJ/m² |
| hardness | Test Condition | Test Method | KOLON KOREA/NOPLA® KE901 |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 110 |
| Mechanical properties | Test Condition | Test Method | KOLON KOREA/NOPLA® KE901 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2900 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 6.4 % |
| tensile strength | 屈服,23°C | ISO 527-2 | 64.0 MPa |
| 23°C | ASTM D638 | 63.0 MPa | |
| Flexural modulus | 23°C | ASTM D790 | 2890 MPa |
| elongation | 断裂,23°C | ASTM D638 | 6.4 % |
| optical performance | Test Condition | Test Method | KOLON KOREA/NOPLA® KE901 |
|---|---|---|---|
| transmissivity | 总计 | ASTM D1003 | 85.0 % |
| Haze ratio | ASTM D1003 | 2.0 % |
| flammability | Test Condition | Test Method | KOLON KOREA/NOPLA® KE901 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | V-2 |
| physical property | Test Condition | Test Method | KOLON KOREA/NOPLA® KE901 |
|---|---|---|---|
| Shrinkage rate | ISO 294-4 | 0.60 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.10 % |
| intrinsic viscosity | 内部方法 | 0.84 dl/g | |
| density | ASTM D792 | 1.34 g/cm³ | |
| ISO 1183 | 1.34 g/cm³ | ||
| melt mass-flow rate | 275°C/2.16kg | ISO 1133 | 12 g/10min |
| Thermal performance | Test Condition | Test Method | KOLON KOREA/NOPLA® KE901 |
|---|---|---|---|
| vicat | ASTM D1525 | 280 °C | |
| melting temperature | ISO 11357-3 | 265 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ASTM D648A | 100 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 115 °C |