PA66 TAROMID A 280 Z1 Taro Plast S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 Z1 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 10 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 100 J/m |
| Electrical performance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 Z1 |
|---|---|---|---|
| dielectric constant | IEC 60250 | 3.80 | |
| Volume resistivity | IEC 60093 | 3E+15 ohms·cm | |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 0 |
| Mechanical properties | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 Z1 |
|---|---|---|---|
| Flexural modulus | ISO 178 | 2500 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 50 % |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| flammability | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 Z1 |
|---|---|---|---|
| UL flame retardant rating | 1.0mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 Z1 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 1.5to1.7 % |
| melt mass-flow rate | 280°C/1.0kg | ISO 1133 | 10 g/10min |
| Water absorption rate | 23°C,24hr | ISO 62 | 1.2 % |
| GranuleHumidity | 内部方法 | <0.15 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 7.0 % |
| density | ISO 1183 | 1.11to1.13 g/cm³ |
| Thermal performance | Test Condition | Test Method | Taro Plast S.p.A./TAROMID A 280 Z1 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 256 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ISO 11359-2 | 7.0E-5到1.0E-4 cm/cm/°C |
| vicat | ISO 306/B50 | 225 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 75.0 °C |
| ball-indentation hardness | 165°C | IEC 60695-10-2 | 通过 |