Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 ECO315 ASCEND USA
Vydyne®
Electrical field、Electronic field、Movable hinge、Spool、Electrical components、Fasteners、printed circuit board、Electrical enclosure、Switch panel、Lighting applications、Electrical appliances、Laptop case、Industrial applications、Automotive sector
low density、Lubricity、Elongated elongation rate、Resistance to stress crac、Good demolding performanc、Ductility、Good flexibility、Halogen-free、Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASCEND USA/ECO315 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak |
| -30°C | ISO179/1eU | NoBreak |
| Electrical performance | Test Condition | Test Method | ASCEND USA/ECO315 |
|---|---|---|---|
| High arc combustion index (HAI) | 0.75mm | UL746 | PLC 0 |
| 0.40mm | UL746 | PLC 0 | |
| Hot wire ignition (HWI) | 3.0mm | UL746 | PLC 3 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL746 | PLC 1 |
| Hot wire ignition (HWI) | 0.40mm | UL746 | PLC 4 |
| 0.75mm | UL746 | PLC 4 | |
| High arc combustion index (HAI) | 3.0mm | UL746 | PLC 0 |
| Hot wire ignition (HWI) | 1.5mm | UL746 | PLC 4 |
| High arc combustion index (HAI) | 1.5mm | UL746 | PLC 0 |
| dielectric strength | 1.00mm | IEC60243 | 13 KV/mm |
| CTI | 3.00mm | IEC60112 | 600 V |
| arc resistance | 3.00mm | ASTMD495 | PLC 5 |
| VolumeResistivity | 0.750mm | IEC60093 | 1E+11 ohms·cm |
| Mechanical properties | Test Condition | Test Method | ASCEND USA/ECO315 |
|---|---|---|---|
| Poisson's ratio | ISO527-2 | 0.40 | |
| Tensile modulus | 23°C | ISO527-2 | 5000 Mpa |
| Flexural modulus | 23°C | ISO178 | 3200 Mpa |
| Tensile strain | 屈服,23°C | ISO527-2 | 5.5 % |
| bending strength | 23°C | ISO178 | 92.0 Mpa |
| Tensile stress | 屈服,23°C | ISO527-2 | 75.0 Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 25 % |
| flammability | Test Condition | Test Method | ASCEND USA/ECO315 |
|---|---|---|---|
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 725 °C |
| Burning wire flammability index | 1.5mm | IEC60695-2-12 | 960 °C |
| 0.75mm | IEC60695-2-12 | 960 °C | |
| 0.40mm | IEC60695-2-12 | 960 °C | |
| UL flame retardant rating | 1.5mm | UL94 | V-0 |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 775 °C |
| Limiting Oxygen Index | ISO4589-2 | 29 % | |
| UL flame retardant rating | 0.40mm | UL94 | V-0 |
| Burning wire flammability index | 3.0mm | IEC60695-2-12 | 960 °C |
| Hot filament ignition temperature | 0.75mm | IEC60695-2-13 | 875 °C |
| 0.40mm | IEC60695-2-13 | 875 °C | |
| UL flame retardant rating | 0.75mm | UL94 | V-0 |
| 3.0mm | UL94 | V-0 |
| physical property | Test Condition | Test Method | ASCEND USA/ECO315 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 2.3 % |
| Shrinkage rate | TD:23°C,2.00mm | ISO294-4 | 1.4 % |
| Water absorption rate | 23°C,24hr | ISO62 | 0.80 % |
| Shrinkage rate | MD:23°C,2.00mm | ISO294-4 | 1.2 % |
| Thermal performance | Test Condition | Test Method | ASCEND USA/ECO315 |
|---|---|---|---|
| TD：23to55°C,2.00mm | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| RTI Str | 0.75mm | UL746 | 100 °C |
| MD：23to55°C,2.00mm | ISO11359-2 | 1.1E-04 cm/cm/°C | |
| RTI Str | 3.0mm | UL746 | 110 °C |
| RTI Elec | 3.0mm | UL746 | 130 °C |
| 1.5mm | UL746 | 130 °C | |
| 0.75mm | UL746 | 130 °C | |
| RTI Str | 1.5mm | UL746 | 100 °C |
| melting temperature | ISO11357-3 | 244 °C | |
| RTI Imp | 1.5mm | UL746 | 85.0 °C |
| RTI Str | 0.40mm | UL746 | 100 °C |
| RTI Imp | 3.0mm | UL746 | 85.0 °C |
| 0.40mm | UL746 | 65.0 °C | |
| 0.75mm | UL746 | 65.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火 | ISO75-2/A | 65.0 °C |
| RTI Elec | 0.40mm | UL746 | 130 °C |
| Heat distortion temperature | 0.45MPa,未退火 | ISO75-2/B | 225 °C |